Laboratory tests and analysis of CIPP epoxy-resin internal liners used in pipelines – part I: comparison of tests and engineering calculations

Tomasz Abel

Tomasz Abel

Wroclaw University of Science and TechnologyPoland
Wyszukaj tego autora
Sciendo|Google Scholar
Abel, Tomasz
  
30 cze 2021
Laboratory tests and analysis of CIPP epoxy-resin internal liners used in pipelines – part I: comparison of tests and engineering calculations's Cover Image
O artykule
Poprzedni artykuł
Następny artykuł
Zacytuj
Pobierz okładkę
Kategoria artykułu: Original Study
Data publikacji: 30 cze 2021
Zakres stron: 169 - 180
Otrzymano: 10 lis 2020
Przyjęty: 31 sty 2021
DOI: https://doi.org/10.2478/sgem-2021-0002
Słowa kluczowe
© 2021 Tomasz Abel, published by Sciendo
This work is licensed under the Creative Commons Attribution 4.0 International License.

Figure 1

Examples of pipe damage: a), b) cracks and structure defects, c) damaged connectors.
Examples of pipe damage: a), b) cracks and structure defects, c) damaged connectors.

Figure 2

Technical conditions according to ATV 143-2; a) technical condition I; b) technical condition II; c) technical condition III; d) technical condition III a [5].
Technical conditions according to ATV 143-2; a) technical condition I; b) technical condition II; c) technical condition III; d) technical condition III a [5].

Figure 3

An overview sketch of the liner's installation.
An overview sketch of the liner's installation.

Figure 4

Illustration of the GWT method for measuring water permeability [30].
Illustration of the GWT method for measuring water permeability [30].

Figure 5

Three-point bending – test scheme.
Three-point bending – test scheme.

Figure 6

Accuracy requirements for the determination of the flexural modulus [18].
Accuracy requirements for the determination of the flexural modulus [18].

Figure 7

Laboratory test of a liner – diameter 200 mm.
Laboratory test of a liner – diameter 200 mm.

Figure 8

Ring stiffness for 200 mm diameter samples.
Ring stiffness for 200 mm diameter samples.

Figure 9

Laboratory test of a liner – diameter 350 mm.
Laboratory test of a liner – diameter 350 mm.

Figure 10

Ring stiffness for 350 mm diameter samples.
Ring stiffness for 350 mm diameter samples.

Figure 11

Laboratory test of a liner – diameter 500 mm.
Laboratory test of a liner – diameter 500 mm.

Figure 12

Ring stiffness for 500 mm diameter samples.
Ring stiffness for 500 mm diameter samples.

Figure 13

The mechanism of the sample's destruction.
The mechanism of the sample's destruction.

Figure 14

Example of a damaged sample.
Example of a damaged sample.

Figure 15

Sample test using the GWT device.
Sample test using the GWT device.

Figure 16

Real and computational ring stiffness for different diameters
Real and computational ring stiffness for different diameters
Język:
Angielski
Częstotliwość wydawania:
4 razy w roku
Dziedziny czasopisma:
Nauki o Ziemi, Nauki o Ziemi, inne, Nauka o materiałach, Kompozyty, Materiały porowate, Fizyka, Mechanika i dynamika płynów
Kanał RSS czasopisma