<abstract xmlns="http://www.w3.org/1999/xhtml"> FeCo fused catalyst was obtained by fusing iron and cobalt oxides with an addition of calcium, aluminium, and potassium oxides (CaO, Al2O3, K2O). An additional amount of potassium oxide was inserted by wet impregnation. Chemical composition of the prepared catalysts was determined with an aid of the XRF method. On the basis of XRD analysis it was found that cobalt was built into the structure of magnetite and solid solution of CoFe2O4 was formed. An increase in potassium content develops surface area of the reduced form of the catalyst, number of adsorption sites for hydrogen, and the ammonia decomposition rate. The nitriding process of the catalyst slows down the ammonia decomposition.</abstract>

FeCo fused catalyst was obtained by fusing iron and cobalt oxides with an addition of calcium, aluminium, and potassium oxides (CaO, Al2O3, K2O). An additional amount of potassium oxide was inserted by wet impregnation. Chemical composition of the prepared catalysts was determined with an aid of the XRF method. On the basis of XRD analysis it was found that cobalt was built into the structure of magnetite and solid solution of CoFe2O4 was formed. An increase in potassium content develops surface area of the reduced form of the catalyst, number of adsorption sites for hydrogen, and the ammonia decomposition rate. The nitriding process of the catalyst slows down the ammonia decomposition.

Characterization of FeCo based catalyst for ammonia decomposition. The effect of potassium oxide

West Pomeranian University of Technology, Szczecin, Institute of Inorganic Chemical Technology and Environmental Engineering, Poland, Pułaskiego 10, 70-322 Szczecin

Polish Journal of Chemical Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

FeCo fused catalyst was obtained by fusing iron and cobalt oxides with an addition of calcium, aluminium, and potassium oxides (CaO, Al2O3, K2O). An additional...

Characterization of FeCo based catalyst for ammonia decomposition. The effect of potassium oxide

Data publikacji: 11 gru 2014

Zakres stron: 111 - 116

DOI: https://doi.org/10.2478/pjct-2014-0080

© by Zofia Lendzion-Bieluń

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.