<p>This paper presents experimental research on expanded clay aggregate concrete. The aim of the investigations was to determine if the pre-wetting of expanded clay aggregate has an effect on the freeze-thaw durability of the expanded clay aggregate concrete. Five concrete series based on the same concrete mix design were made and tested. The degree of pre-wetting of the aggregate was varied: dry aggregate was used in the first series, aggregate with a moisture content of 10% was used in series IA and IB and aggregate with a moisture content of 25% was used in series IIA and IIB. Also the approach to the production process was varied: in series A the water contained in the aggregate was taken into account in the global water-cement ratio (consequently a reduced amount of water was added to the mix), whereas in series B the nominal amount of water was added to the mix (as in the case of dry aggregate). The freeze-thaw resistance criterion was based on the assessment of the decrease of compressive strength and increase in weight loss after exposure to freeze-thaw cycles. The expanded clay aggregate concrete's strength and mass decrements caused by freeze-thaw cycling were used as the measure of its freeze-thaw resistance. The investigations have shown that the pre-wetting of expanded clay aggregate has an effect on the freeze-thaw durability of the expanded clay aggregate concrete. The differences of concrete compressive strength decrease related to freeze-thaw durability may be 2 to 5 times greater when inadequate method of calculating mixing water for concrete is used.</p>
</abstract>

This paper presents experimental research on expanded clay aggregate concrete. The aim of the investigations was to determine if the pre-wetting of expanded clay aggregate has an effect on the freeze-thaw durability of the expanded clay aggregate concrete. Five concrete series based on the same concrete mix design were made and tested. The degree of pre-wetting of the aggregate was varied: dry aggregate was used in the first series, aggregate with a moisture content of 10% was used in series IA and IB and aggregate with a moisture content of 25% was used in series IIA and IIB. Also the approach to the production process was varied: in series A the water contained in the aggregate was taken into account in the global water-cement ratio (consequently a reduced amount of water was added to the mix), whereas in series B the nominal amount of water was added to the mix (as in the case of dry aggregate). The freeze-thaw resistance criterion was based on the assessment of the decrease of compressive strength and increase in weight loss after exposure to freeze-thaw cycles. The expanded clay aggregate concrete's strength and mass decrements caused by freeze-thaw cycling were used as the measure of its freeze-thaw resistance. The investigations have shown that the pre-wetting of expanded clay aggregate has an effect on the freeze-thaw durability of the expanded clay aggregate concrete. The differences of concrete compressive strength decrease related to freeze-thaw durability may be 2 to 5 times greater when inadequate method of calculating mixing water for concrete is used.

The effect of the pre-wetting of expanded clay aggregate on the freeze-thaw resistance of the expanded clay aggregate concrete

Wroclaw University of Science and Technology: Politechnika Wroclawska

Wroclaw University of Science and Technology, Politechnika Wroclawska

Studia Geotechnica et Mechanica

This work is licensed under the Creative Commons Attribution 4.0 International License.

This paper presents experimental research on expanded clay aggregate concrete. The aim of the investigations was to determine if the pre-wetting of expanded...

The effect of the pre-wetting of expanded clay aggregate on the freeze-thaw resistance of the expanded clay aggregate concrete

Article Category: Original Study

Pubblicato online: 30 giu 2021

Pagine: 65 - 73

Ricevuto: 21 ott 2020

Accettato: 19 nov 2020

DOI: https://doi.org/10.2478/sgem-2020-0011

Parole chiave
lightweight concrete, freeze-thaw resistance, aggregate pre-wetting

© 2021 Michał Piotr Musiał et al., published by Sciendo

This work is licensed under the Creative Commons Attribution 4.0 International License.

The effect of the pre-wetting of expanded clay aggregate on the freeze-thaw resistance of the expanded clay aggregate concrete

Article Category: Original Study

Pubblicato online: 30 giu 2021

Pagine: 65 - 73

Ricevuto: 21 ott 2020

Accettato: 19 nov 2020

DOI: https://doi.org/10.2478/sgem-2020-0011

Parole chiavelightweight concrete, freeze-thaw resistance, aggregate pre-wetting

© 2021 Michał Piotr Musiał et al., published by Sciendo

This work is licensed under the Creative Commons Attribution 4.0 International License.

Parole chiave
lightweight concrete, freeze-thaw resistance, aggregate pre-wetting