<abstract xmlns="http://www.w3.org/1999/xhtml"><p>The positron annihilation method was used to study the formation of defects in titanium samples during their corrosion in the vapor of a 3% HCl solution. In particular, the distribution of defects depending on the distance from the corroding surface and the impact of an external magnetic field on the concentration of vacancies forming during the corrosion of titanium layers close to the surface were determined.</p></abstract>

The positron annihilation method was used to study the formation of defects in titanium samples during their corrosion in the vapor of a 3% HCl solution. In particular, the distribution of defects depending on the distance from the corroding surface and the impact of an external magnetic field on the concentration of vacancies forming during the corrosion of titanium layers close to the surface were determined.

Investigation of corrosion defects in titanium by positron annihilation

Institute of Physics, Opole University, 48 Oleska Str., 45-052 Opole, Poland, Tel.: +48 77 452 7250, Fax: +48 77 452 7290

Nukleonika

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Investigation of corrosion defects in titanium by positron annihilation"}

The positron annihilation method was used to study the formation of defects in titanium samples during their corrosion in the vapor of a 3% HCl solution. In...

Investigation of corrosion defects in titanium by positron annihilation

Online veröffentlicht: 01. Dez. 2015

Seitenbereich: 755 - 758

Eingereicht: 19. Juni 2015

Akzeptiert: 01. Sept. 2015

DOI: https://doi.org/10.1515/nuka-2015-0136

Schlüsselwörter
positron annihilation spectroscopy, corrosion defects

© 2015 Ryszard Pietrzak et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Investigation of corrosion defects in titanium by positron annihilation

Online veröffentlicht: 01. Dez. 2015

Seitenbereich: 755 - 758

Eingereicht: 19. Juni 2015

Akzeptiert: 01. Sept. 2015

DOI: https://doi.org/10.1515/nuka-2015-0136

Schlüsselwörterpositron annihilation spectroscopy, corrosion defects

© 2015 Ryszard Pietrzak et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
positron annihilation spectroscopy, corrosion defects