<abstract xmlns="http://www.w3.org/1999/xhtml"><p>The positron annihilation method was used to study the formation of defects in titanium samples during their corrosion in the vapor of a 3% HCl solution. In particular, the distribution of defects depending on the distance from the corroding surface and the impact of an external magnetic field on the concentration of vacancies forming during the corrosion of titanium layers close to the surface were determined.</p></abstract>

The positron annihilation method was used to study the formation of defects in titanium samples during their corrosion in the vapor of a 3% HCl solution. In particular, the distribution of defects depending on the distance from the corroding surface and the impact of an external magnetic field on the concentration of vacancies forming during the corrosion of titanium layers close to the surface were determined.

Investigation of corrosion defects in titanium by positron annihilation

Institute of Physics, Opole University, 48 Oleska Str., 45-052 Opole, Poland, Tel.: +48 77 452 7250, Fax: +48 77 452 7290

Nukleonika

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Investigation of corrosion defects in titanium by positron annihilation"}

The positron annihilation method was used to study the formation of defects in titanium samples during their corrosion in the vapor of a 3% HCl solution. In...

Investigation of corrosion defects in titanium by positron annihilation

Pubblicato online: 01 dic 2015

Pagine: 755 - 758

Ricevuto: 19 giu 2015

Accettato: 01 set 2015

DOI: https://doi.org/10.1515/nuka-2015-0136

Parole chiave
positron annihilation spectroscopy, corrosion defects

© 2015 Ryszard Pietrzak et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Investigation of corrosion defects in titanium by positron annihilation

Pubblicato online: 01 dic 2015

Pagine: 755 - 758

Ricevuto: 19 giu 2015

Accettato: 01 set 2015

DOI: https://doi.org/10.1515/nuka-2015-0136

Parole chiavepositron annihilation spectroscopy, corrosion defects

© 2015 Ryszard Pietrzak et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Parole chiave
positron annihilation spectroscopy, corrosion defects