Preparation of ternary (35 – x)Sb2O3–xBi2O3–65P2O5 glasses for lead-free glass application

Published Online: 08 May 2020
Volume & Issue: Volume 38 (2020) - Issue 1 (March 2020)
Page range: 28 - 33
Received: 04 May 2017
Accepted: 24 Oct 2018
Journal Details
License
Format
Journal
eISSN
2083-134X
First Published
16 Apr 2011
Publication timeframe
4 times per year
Languages
English
Abstract

Glasses composed of ternary components (35 – x)Sb2O3–xBi2O3–65P2O5 (0 ⩽ x ⩽ 20 mol%) have been prepared and investigated as a potential alternative to lead-free glass for low temperature applications. Their structural properties were studied by Infrared Spectroscopy IR and Differential Thermal Analysis DTA. Results from the IR showed that Sb3+ and Bi3+ were responsible for glass network structure, which was supported by the diversification of density ρ and molar volume Vm with an increasing amount of Bi2O3. Glass transition temperature Tg, thermal stability, and coefficient of thermal expansion increased after substitution of Bi2O3 for Sb2O3 within the range of 0 mol% to 20 mol%. The water durability decreased and then increased; it could be attributed to the corrosion resistant P–O–Sb bonds. A typical sample of 25Sb2O3–10Bi2O3–65P2O5 possesses excellent properties and can be a promising candidate for further applications.

Keywords

[1] Gu S.Y., Wang Z.Q., Jiang S.W., Lin H., Ceram. Int., 40 (2014), 7643.Search in Google Scholar

[2] Huang B., Gan W.P., Guo G.G., Li Y, Liu X., Ceram. Int., 40 (2014), 393.10.1016/j.ceramint.2013.06.014Search in Google Scholar

[3] Bobkov A.N.M., J. Glass. Phys. Chem. Glasses, 38 (2012), 180.10.1134/S108765961201004XSearch in Google Scholar

[4] Massera J., Bourhis K., Petit L., Couzi M., Hupa L., Hupa M., Videau J. J., Cardinal T.J., J. Phys. Chem. Solids, 74 (2013), 121.10.1016/j.jpcs.2012.08.010Search in Google Scholar

[5] Li H. Y., Zhu Z.L., Yang F.L., J. Int. J. Min. Met. Mater., 19 (2012), 628.Search in Google Scholar

[6] Kim H.J., Je S.Y., Ju Y.W., Baek J.H., Jeong J.K., Phys. Status Solidi R, 8 (2014), 924.10.1002/pssr.201409402Search in Google Scholar

[7] Ciceo R.L., Trandafir D.L., Radu T., Ponta O., Simon V., Ceram. Int., 40 (2014), 9517.10.1016/j.ceramint.2014.02.025Search in Google Scholar

[8] Tiwari A.N., Subbarao E.C., J. Am. Ceram. Soc., 53 (1970), 258.10.1111/j.1151-2916.1970.tb12088.xSearch in Google Scholar

[9] Zhang B., Chen Q., Song L., Li H, Hou F., J. Am. Ceram. Soc., 91 (2008), 2036.10.1111/j.1551-2916.2008.02339.xSearch in Google Scholar

[10] Qi Y.J., Wang Z.Q., Zhai S.R., Mater. Sci. -Poland, 32 (2014), 414.10.2478/s13536-014-0214-0Search in Google Scholar

[11] Efimov A.M., J. Non-Cryst. Solids, 209 (1997), 213.10.1016/S0022-3093(97)00010-0Search in Google Scholar

[12] Zhang B., Chen Q., Song L., J. Non-Cryst. Solids, 354 (2008), 1948.10.1016/j.jnoncrysol.2007.11.007Search in Google Scholar

[13] Hafid M., Jermoumi T., Toreis N., Ghailassi T., Mater. Lett., 56 (2002), 486.10.1016/S0167-577X(02)00537-2Search in Google Scholar

[14] Tang G., Li J., Lu A.X., J. Mater. Rev., 1 (2012), 122.Search in Google Scholar

[15] Chahine A., Et-Tabirou M., Pascal J.L., J. Mater. Lett., 58 (2004), 2776.10.1016/j.matlet.2004.04.010Search in Google Scholar

[16] Menaa B., Mizuno M., Takahashi M., Tokuda Y., Yoko T., J. Solid State Chem., 179 (2006), 492.10.1016/j.jssc.2005.11.001Search in Google Scholar

[17] Golovin A.I., Pavlovski V.K., Shchavelev O.S., Glass. Ceram., 49 (1993), 513.10.1007/BF00678911Search in Google Scholar

[18] Zhang B., Chen Q., Song L., Li H., Zhang J., J. Non-Cryst. Solids, 354 (2008), 1948.10.1016/j.jnoncrysol.2007.11.007Search in Google Scholar

[19] Li H.Y., Zhu Z.L., Yang F.L., Zhang W.D., Vac. Sci., 3 (2012), 43.Search in Google Scholar

[20] Wang M.Q., Xiong G.H., Zhang R.C., J. China Ceram. Soc., 20 (1992), 457.Search in Google Scholar

Recommended articles from Trend MD

Plan your remote conference with Sciendo