Specimen | Laying angle |
---|---|
A | [0°]8 |
B | [0°/45°/90°/−45°]s |
C | [0°/90°]4 |
D | [45°/−45°]4 |
Group | Laying angle | Failure load (N) | Bending strength (MPa) |
---|---|---|---|
A | [0°]8 | 762.67 | 64.63 |
B | [0°/45°/90°/−45°]s | 454.23 | 38.49 |
C | [0°/90°]4 | 355.80 | 30.15 |
D | [45°/−45°]4 | 92.47 | 7.84 |
Carbon yarn weight (g/m2) | Resin content (g/m2) | Resin weight (g/m2) | Gross weight (g/m2) | Thickness ( |
---|---|---|---|---|
150 | 32 | 71 | 221 | 0.150 |
Density (kg/m3) | Elastic modulus (MPa) | Poisson’s ratio | Shear modulus (MPa) | Tensile strength (MPa) | Compressive strength (MPa) | Shear strength (MPa) | Elongation at break (%) |
---|---|---|---|---|---|---|---|
75 | 92 | 0.3 | 29 | 2.8 | 1.5 | 1.3 | 3.0 |