Synthesis route | IR frequency bands[cm−1] | |
---|---|---|
ν1 | ν2 | |
CSG | 580 | 405 |
SGC | 592 | 400 |
Co-P | 586 | 401 |
Synthesis route | Band gap [eV] | Crystallite size [nm] |
---|---|---|
CSG | 5.9 | 70.73 |
SGC | 5.2 | 26.71 |
Co-P | 5.8 | 35.35 |
Preparation technique | Crystallite size [nm] | Saturation magnetization MS [emu/g] | Remanence MR [emu/g] | Coercivity HC [Oe] |
---|---|---|---|---|
CSG | 70.73 | 36.61 | 8.252 | 72.3 |
SGC | 26.71 | 3.6691 | 0.857 | 230 |
Co-P | 35.35 | 28.58 | 11.341 | 201 |
Preparation technique | Annealing temperature [°C] | Crystallite size [nm] | X-ray density [g/cc] | Lattice constant [Å] |
---|---|---|---|---|
CSG | 1000 | 70.73 | 5.6049 | 8.2215 |
SGC | 1000 | 26.71 | 4.8974 | 8.3253 |
Co-P | 1000 | 35.35 | 5.3980 | 8.5998 |