Sample | L* | a* | b* | C* | h |
---|---|---|---|---|---|
CSFL3 | 66.10 ± 1.67 | 4.63 ± 0.12 | 22.73 ± 0.58 | 23.19 ± 0.82 | 78.52 ± 2.77 |
CSLF7 | 55.67 ± 1.54 | 8.21 ± 0.23 | 25.57 ± 0.71 | 26.86 ± 1.01 | 72.25 ± 2.72 |
CSFL14 | 59.63 ± 1.33 | 11.45 ± 0.25 | 32.88 ± 0.73 | 34.82 ± 1.12 | 70.83 ± 2.28 |
CSFL12 | 56.72 ± 1.60 | 9.23 ± 0.26 | 26.69 ± 0.75 | 28.24 ± 1.08 | 70.95 ± 2.71 |
CSFL11 | 64.25 ± 1.52 | 3.46 ± 0.08 | 20.32 ± 0.48 | 20.62 ± 0.69 | 80.39 ± 2.70 |
Sample | k-value | Qβ (Gy) | qβ (Gy) |
---|---|---|---|
CSLF2 | 0.259 ± 0.011 | 2.09 ± 0.19 | 0.13 ± 0.02 |
CSLF6 | 0.232 ± 0.018 | 2.87 ± 0.23 | 0.05 ± 0.01 |
CSLF10 | 0.220 ± 0.010 | 3.18 ± 0.28 | 0.09 ± 0.02 |
Sample | Material | Technique | Method | ED (Gy) | Annual dose rate (mGy/a) | Age/2016 (a) | Age (AD) |
---|---|---|---|---|---|---|---|
CSFL2 | TL | Added dose | 2.22 ± 0.19 | 11.43 ± 0.85 | 194 ± 22 | 1822 ±22 | |
CSFL3 | OSL | SAR | 1.17 ± 0.10 | 5.41 ± 0.37 | 216 ± 24 | 1800 ±24 | |
CSFL6 | TL | Added dose | 2.92 ± 0.23 | 8.62 ± 0.66 | 339 ± 37 | 1677 ± 37 | |
CSFL7 | OSL | SAR | 2.03 ± 0.21 | 6.67 ± 0.47 | 304 ± 38 | 1712 ± 38 | |
CSFL10 | TL | Added dose | 3.27 ± 0.28 | 9.44 ± 0.63 | 346 ± 38 | 1670 ± 38 | |
CSFL11 | OSL | SAR | 1.13 ± 0.11 | 5.76 ± 0.37 | 196 ± 23 | 1820 ± 23 | |
CSFL12 | OSL | SAR | 2.41 ± 0.15 | 7.47 ± 0.44 | 322 ± 28 | 1694 ± 28 | |
CSFL14 | OSL | SAR | 2.61 ± 0.18 | 7.81 ± 0.48 | 344 ± 31 | 1672 ± 31 |
Sample | Material | W | Dαint(mGy/a) | Dβint(mGy/a) | Denv(mGy/a) |
---|---|---|---|---|---|
CSFL2 | 0.16 ± 0.01 | 29.65 ± 1.25 | 3.22 ± 0.08 | 1.22 ± 0.05 | |
CSFL3 | 0.21 ± 0.02 | 22.71 ± 0.93 | 1.71 ± 0.04 | ||
CSFL6 | 0.15 ± 0.01 | 22.24 ± 0.95 | 2.53 ± 0.06 | 1.37 ± 0.05 | |
CSFL7 | 0.22 ± 0.02 | 22.36 ± 0.90 | 2.18 ± 0.05 | ||
CSFL10 | 0.17 ± 0.01 | 24.95 ± 1.01 | 2.94 ± 0.07 | 1.57 ± 0.05 | |
CSFL11 | 0.27 ± 0.02 | 21.38 ± 0.89 | 1.80 ± 0.05 | ||
CSFL12 | 0.25 ± 0.02 | 23.31 ± 0.39 | 2.87 ± 0.06 | 1.75 ± 0.05 | |
CSFL14 | 0.23 ± 0.02 | 24.78 ± 0.28 | 2.86 ± 0.05 | 1.65 ± 0.05 |
Sample | Qz | K-felds | Na-plag | Cal | Dolo | Phyl | Aggregate (A) | Binder (B) | A/B Ratio |
---|---|---|---|---|---|---|---|---|---|
CSFL3 | 65 | 21 | 1 | 13 | * | * | 86 | 13 | 6.62 |
CSFL7 | 65 | 5 | * | 26 | 2 | 2 | 70 | 26 | 2.69 |
CSFL11 | 71 | 14 | 1 | 13 | 1 | * | 85 | 13 | 6.54 |
CSFL12 | 59 | 12 | 10 | 18 | 1 | * | 71 | 18 | 3.94 |
CSFL14 | 66 | 11 | 1 | 21 | 1 | * | 77 | 21 | 3.67 |
Sampling point (floor 2) | |||
---|---|---|---|
Sample | Material | Architectural element | Height height above planking level |
CSLF2 | Brick | Arc (east) | 350 |
CSLF3 | Mortar | ||
CSLF6 | Brick | Arc (south) | 80 |
CSLF7 | Mortar | ||
CSLF10 | Brick | Arc (west) | 235 |
CSLF11 | Mortar | ||
CSLF12 | Mortar | Wall (west) | 145 |
CSLF14 | Mortar | Wall (north) | 150 |
Sample | Plateau ED range (°C) | Ph temperature (°C) |
---|---|---|
CSLF3 | 180–220 | 200 |
CSLF7 | 180–240 | 210 |
CSLF11 | 180–220 | 200 |
CSLF12 | 180–220 | 200 |
CSLF14 | 180–240 | 210 |
Sample | Number of aliquots ( | k-value | ED Central Value from Radial Plot | Mean ED from ED frequency distributions |
---|---|---|---|---|
CSFL3 | 39 | 0.125 ± 0.010 | 1.17 0.10 | 1.18 0.18 |
CSFL7 | 47 | 0.161 ± 0.012 | 2.03 0.21 | 2.02 0.26 |
CSFL11 | 41 | 0.134 ± 0.010 | 1.13 0.11 | 1.12 0.17 |
CSFL12 | 38 | 0.148 ± 0.010 | 2.41 0.15 | 2.42 0.22 |
CSFL14 | 44 | 0.157 ± 0.010 | 2.61 0.18 | 2.63 0.25 |
Sample | Material | 238U/226Ra | U (ppm) | Th (ppm) | K (%) |
---|---|---|---|---|---|
CSFL2 | 1.03 ± 0.11 | 4.54 ± 0.22 | 23.26 ± 1.49 | 2.46 ± 0.07 | |
CSFL3 | 0.97 ± 0.08 | 3.76 ± 0.18 | 16.57 ± 1.07 | 0.90 ± 0.03 | |
CSFL6 | 1.02 ± 0.12 | 3.26 ± 0.16 | 18.00 ± 1.15 | 2.00 ± 0.06 | |
CSFL7 | 0.97 ± 0.09 | 3.91 ± 0.19 | 15.70 ± 1.00 | 1.51 ± 0.05 | |
CSFL10 | 0.98 ± 0.10 | 4.30 ± 0.21 | 17.75 ± 1.14 | 2.33 ± 0.07 | |
CSFL11 | 1.05 ± 0.08 | 3.40 ± 0.16 | 16.30 ± 1.04 | 1.10 ± 0.03 | |
CSFL12 | 0.99 ± 0.08 | 3.52 ± 0.06 | 18.48 ± 0.49 | 2.37 ± 0.07 | |
CSFL14 | 0.97 ± 0.10 | 3.70 ± 0.06 | 19.80 ± 0.31 | 2.27 ± 0.07 |