<p>During the process of regeneration of machine parts, certain phenomena occur that have a significant impact on the loss of their working ability. Hereditary properties are expressed by the interdependence of geometric and physical-mechanical-metallurgical parameters of gear teeth created during the technological operations of regeneration of worn teeth by hard-facing. The influence of the type of additional material (electrodes and their combinations) on the tribological characteristics of welded gear teeth was considered, whereby the so-called hard additional materials were applied. Those are the additional materials that give the required surface hardness of the teeth without subsequent thermal or thermochemical treatment. This research did not involve the regeneration of specific worn gears removed from machine systems, but the new gears were made, which were then damaged and then regenerated by hard-facing using the shielded metal arc welding (SMAW) procedure. Thus, all the tested gears were made of the same material, belonged to one batch and were machined on the same machines with the same machining regimes. The tests were performed on samples made of 20MnCr5 steel for cementation, on a tribometer by the “block on disc” method, which was designed to simulate the operating conditions of coupled teeth of concrete gears in the exploitation conditions. Based on the conducted tribological tests, the average coefficients of friction and topography of the surfaces were determined by measuring the wear trace and it was defined which additional materials give the best tribological characteristics of the surfaces of gears regenerated by hard-facing.</p>
</abstract>

During the process of regeneration of machine parts, certain phenomena occur that have a significant impact on the loss of their working ability. Hereditary properties are expressed by the interdependence of geometric and physical-mechanical-metallurgical parameters of gear teeth created during the technological operations of regeneration of worn teeth by hard-facing. The influence of the type of additional material (electrodes and their combinations) on the tribological characteristics of welded gear teeth was considered, whereby the so-called hard additional materials were applied. Those are the additional materials that give the required surface hardness of the teeth without subsequent thermal or thermochemical treatment. This research did not involve the regeneration of specific worn gears removed from machine systems, but the new gears were made, which were then damaged and then regenerated by hard-facing using the shielded metal arc welding (SMAW) procedure. Thus, all the tested gears were made of the same material, belonged to one batch and were machined on the same machines with the same machining regimes. The tests were performed on samples made of 20MnCr5 steel for cementation, on a tribometer by the “block on disc” method, which was designed to simulate the operating conditions of coupled teeth of concrete gears in the exploitation conditions. Based on the conducted tribological tests, the average coefficients of friction and topography of the surfaces were determined by measuring the wear trace and it was defined which additional materials give the best tribological characteristics of the surfaces of gears regenerated by hard-facing.

Influence of different hard-facing procedures on quality of surfaces of regenerated gears

Department of Production Engineering and Safety

Production Engineering Archives

This work is licensed under the Creative Commons Attribution-ShareAlike 4.0 International License.

During the process of regeneration of machine parts, certain phenomena occur that have a significant impact on the loss of their working ability. Hereditary...

Influence of different hard-facing procedures on quality of surfaces of regenerated gears

Data publikacji: 20 lis 2021

Zakres stron: 257 - 264

Otrzymano: 19 sie 2021

Przyjęty: 26 wrz 2021

DOI: https://doi.org/10.30657/pea.2021.27.34

Słowa kluczowe
regeneration, hard-facing, gear, tribological properties, friction coefficient

© 2021 Ružica R. Nikolić et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-ShareAlike 4.0 International License.

Influence of different hard-facing procedures on quality of surfaces of regenerated gears

Data publikacji: 20 lis 2021

Zakres stron: 257 - 264

Otrzymano: 19 sie 2021

Przyjęty: 26 wrz 2021

DOI: https://doi.org/10.30657/pea.2021.27.34

Słowa kluczoweregeneration, hard-facing, gear, tribological properties, friction coefficient

© 2021 Ružica R. Nikolić et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-ShareAlike 4.0 International License.

Słowa kluczowe
regeneration, hard-facing, gear, tribological properties, friction coefficient