<abstract xmlns="http://www.w3.org/1999/xhtml">The paper presents the results of low and high frequency fatigue tests carried out on nodular cast iron. The specimens of synthetic nodular cast irons from three different melts were studied in the high cycle fatigue region (from 105 to 108 cycles) using fatigue experimental equipments for low and high frequency cyclic loading. Low frequency fatigue tests were carried out at frequency f ≈ 120 Hz using the fatigue experimental machine Zwick/Roell Amsler 150HFP 5100; high frequency fatigue tests were carried out at frequency f ≈ 20 kHz using the ultrasonic fatigue testing device KAUP-ZU. Both fatigue tests were realised at sinusoidal cyclic push-pull loading (stress ratio R = −1) at ambient temperature (T = 20 ± 5 °C).</abstract>

The paper presents the results of low and high frequency fatigue tests carried out on nodular cast iron. The specimens of synthetic nodular cast irons from three different melts were studied in the high cycle fatigue region (from 105 to 108 cycles) using fatigue experimental equipments for low and high frequency cyclic loading. Low frequency fatigue tests were carried out at frequency f ≈ 120 Hz using the fatigue experimental machine Zwick/Roell Amsler 150HFP 5100; high frequency fatigue tests were carried out at frequency f ≈ 20 kHz using the ultrasonic fatigue testing device KAUP-ZU. Both fatigue tests were realised at sinusoidal cyclic push-pull loading (stress ratio R = −1) at ambient temperature (T = 20 ± 5 °C).

Comparison of low and high frequency fatigue tests

Faculty of Mechanical Engineering, Department of Materials Engineering

Production Engineering Archives

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Comparison of low and high frequency fatigue tests"}

The paper presents the results of low and high frequency fatigue tests carried out on nodular cast iron. The specimens of synthetic nodular cast irons from...

Comparison of low and high frequency fatigue tests

Data publikacji: 28 sty 2020

Zakres stron: 14 - 17

Otrzymano: 31 paź 2017

Przyjęty: 30 gru 2017

DOI: https://doi.org/10.30657/pea.2017.17.03

Słowa kluczowe
fatigue test, low frequency cyclic loading, high frequency cyclic loading, nodular cast iron

© 2017 Alan Vaško et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Comparison of low and high frequency fatigue tests

Data publikacji: 28 sty 2020

Zakres stron: 14 - 17

Otrzymano: 31 paź 2017

Przyjęty: 30 gru 2017

DOI: https://doi.org/10.30657/pea.2017.17.03

Słowa kluczowefatigue test, low frequency cyclic loading, high frequency cyclic loading, nodular cast iron

© 2017 Alan Vaško et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Słowa kluczowe
fatigue test, low frequency cyclic loading, high frequency cyclic loading, nodular cast iron