<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>In this paper, some results are presented from experiments concerning partial discharge (PD) behaviour of epoxy resin samples having 3 <italic>wt</italic>% nano- and 3 <italic>wt</italic>% micro-fillers, as well as epoxy samples having 3 <italic>wt</italic>%<italic>and</italic>1 <italic>wt</italic>% nanoparticles. The nano- and micro-fillers were TiO<sub>2</sub> (titania). The main idea is to see whether a sample with PD at its inception voltage, still presents some tendency to charging effects below inception. An effort is being made to relate the present work with previous publications on the same main idea, as well as to previous research performed recently at Xian Jiaotong University, State Key Laboratory of Electrical Insulation and Power Equipment. It is indicated that with the samples investigated, although on some occasions random charging phenomena were observed below the inception voltage, it was not noted the same behaviour as with pure epoxy samples. Finally, a discussion ensues as to the definitions of the phenomena taking place below inception voltage.</p></abstract>

In this paper, some results are presented from experiments concerning partial discharge (PD) behaviour of epoxy resin samples having 3 wt% nano- and 3 wt% micro-fillers, as well as epoxy samples having 3 wt%and1 wt% nanoparticles. The nano- and micro-fillers were TiO2 (titania). The main idea is to see whether a sample with PD at its inception voltage, still presents some tendency to charging effects below inception. An effort is being made to relate the present work with previous publications on the same main idea, as well as to previous research performed recently at Xian Jiaotong University, State Key Laboratory of Electrical Insulation and Power Equipment. It is indicated that with the samples investigated, although on some occasions random charging phenomena were observed below the inception voltage, it was not noted the same behaviour as with pure epoxy samples. Finally, a discussion ensues as to the definitions of the phenomena taking place below inception voltage.

Preliminary Experimental Work on Nanocomposite Polymers: Small Partial Discharges at Inception Voltage, The Existence of Possible Charging Mechanisms Below Inception Voltage and the Problem of Definitions

State Key Laboratory of Electrical Insulation and Power Equipment (SKLEIPE), School of Electrical Engineering, Xian Jiaotong Universiy, Xian, Shaanxi 710049, P. R. China

Journal of Electrical Engineering

In this paper, some results are presented from experiments concerning partial discharge (PD) behaviour of epoxy resin samples having 3 wt% nano- and 3 wt%...

Preliminary Experimental Work on Nanocomposite Polymers: Small Partial Discharges at Inception Voltage, The Existence of Possible Charging Mechanisms Below Inception Voltage and the Problem of Definitions

Data publikacji: 20 kwi 2012

Zakres stron: 109 - 114

DOI: https://doi.org/10.2478/v10187-012-0016-8

Słowa kluczowe
small discharges, charging effects, nanocomposites, nanofillers

This content is open access.

Preliminary Experimental Work on Nanocomposite Polymers: Small Partial Discharges at Inception Voltage, The Existence of Possible Charging Mechanisms Below Inception Voltage and the Problem of Definitions

Data publikacji: 20 kwi 2012

Zakres stron: 109 - 114

DOI: https://doi.org/10.2478/v10187-012-0016-8

Słowa kluczowesmall discharges, charging effects, nanocomposites, nanofillers

This content is open access.

Słowa kluczowe
small discharges, charging effects, nanocomposites, nanofillers