<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>Zinc oxide derived from processing of the slime obtained in an industrial process of electrolytic zinc obtaining was leached with the aqueous sulfuric acid solution. The effect of temperature and time on the extent of leaching was determined. The conditions lead to zinc recovery of about 90%. It was found that the extent of arsenic leaching did not depend upon the time and temperature of leaching. Next the conditions of the solution purification procedure were determined. It was found that jarosite formation as well as the degree of arsenic removal is connected with trivalent iron concentration in the solution.</p></abstract>

Zinc oxide derived from processing of the slime obtained in an industrial process of electrolytic zinc obtaining was leached with the aqueous sulfuric acid solution. The effect of temperature and time on the extent of leaching was determined. The conditions lead to zinc recovery of about 90%. It was found that the extent of arsenic leaching did not depend upon the time and temperature of leaching. Next the conditions of the solution purification procedure were determined. It was found that jarosite formation as well as the degree of arsenic removal is connected with trivalent iron concentration in the solution.

Precipitation of jarosite as a purifying procedure of the solution obtained after leaching of zinc secondary material

Faculty of Engineering and Chemical Technology, Cracow University of Technology, ul. Warszawska 24, 31-155 Kraków, Poland

BOL-THERM Sp. z o.o., ul. Kolejowa 37, 32-332 Bukowno, Poland

Polish Journal of Chemical Technology

Zinc oxide derived from processing of the slime obtained in an industrial process of electrolytic zinc obtaining was leached with the aqueous sulfuric acid...

Precipitation of jarosite as a purifying procedure of the solution obtained after leaching of zinc secondary material

Data publikacji: 28 gru 2010

Zakres stron: 36 - 39

DOI: https://doi.org/10.2478/v10026-010-0047-5

Słowa kluczowe
jarosite, leaching, purification of solution, secondary material

This content is open access.

Precipitation of jarosite as a purifying procedure of the solution obtained after leaching of zinc secondary material

Data publikacji: 28 gru 2010

Zakres stron: 36 - 39

DOI: https://doi.org/10.2478/v10026-010-0047-5

Słowa kluczowejarosite, leaching, purification of solution, secondary material