<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>Duck eggs are one of the most versatile cooking ingredients in which residue eggshells are discarded. Raw duck eggshells were calcined at temperatures between 300 to 900 °C, for 1, 3, and 5 h. Both the raw and calcined duck eggshells were characterized by FTIR, STA, XRD, XRF, TEM, BET, a particle size analyzer, and an impedance analyzer. The proper calcination conditions are: 900 °C and 1 h, yielding calcium oxide with a purity of 99.06 % w/w. The calcium carbonate of the rhombohedral form (CaCO3) transforms completely into the calcium oxide or lime of the face centered cubic form (CaO) at 900 °C, as shown by XRD diffraction patterns. The transmission electron microscopy (TEM) images of the calcium oxide reveal a moderately good dispersion of nearly uniform particles. The calcium oxide has a white color, a spherical shape, high porosity, and narrow particles size distribution. The percentage of ceramic yield of the calcium oxide is 53.53, as measured by STA (TG-DTA-DTG). The calcium oxide has a N2 adsorption-desorption isotherm indicating the meso-porosity range. The dielectric constant and the electrical conductivity of the calcined calcium oxide are 35 and 1:0×10−6(Ω·m)−1, respectively, at the frequency of 500 Hz.</p></abstract>

Duck eggs are one of the most versatile cooking ingredients in which residue eggshells are discarded. Raw duck eggshells were calcined at temperatures between 300 to 900 °C, for 1, 3, and 5 h. Both the raw and calcined duck eggshells were characterized by FTIR, STA, XRD, XRF, TEM, BET, a particle size analyzer, and an impedance analyzer. The proper calcination conditions are: 900 °C and 1 h, yielding calcium oxide with a purity of 99.06 % w/w. The calcium carbonate of the rhombohedral form (CaCO3) transforms completely into the calcium oxide or lime of the face centered cubic form (CaO) at 900 °C, as shown by XRD diffraction patterns. The transmission electron microscopy (TEM) images of the calcium oxide reveal a moderately good dispersion of nearly uniform particles. The calcium oxide has a white color, a spherical shape, high porosity, and narrow particles size distribution. The percentage of ceramic yield of the calcium oxide is 53.53, as measured by STA (TG-DTA-DTG). The calcium oxide has a N2 adsorption-desorption isotherm indicating the meso-porosity range. The dielectric constant and the electrical conductivity of the calcined calcium oxide are 35 and 1:0×10−6(Ω·m)−1, respectively, at the frequency of 500 Hz.

Preparation and properties of calcium oxide from eggshells via calcination

Center for Advanced Studies in Industrial Technology and The Materials Engineering Department, Faculty of Engineering, Kasetsart University, Bangkok, 10900, Thailand

The Petroleum and Petrochemical College, Chulalongkorn University, Bangkok, 10330, Thailand

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Preparation and properties of calcium oxide from eggshells via calcination"}

Duck eggs are one of the most versatile cooking ingredients in which residue eggshells are discarded. Raw duck eggshells were calcined at temperatures between...

Preparation and properties of calcium oxide from eggshells via calcination

Data publikacji: 14 gru 2012

Zakres stron: 313 - 322

DOI: https://doi.org/10.2478/s13536-012-0055-7

Słowa kluczowe
calcium oxide, pyrolysis, specific surface area, phase transformation

© 2012 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Preparation and properties of calcium oxide from eggshells via calcination

Data publikacji: 14 gru 2012

Zakres stron: 313 - 322

DOI: https://doi.org/10.2478/s13536-012-0055-7

Słowa kluczowecalcium oxide, pyrolysis, specific surface area, phase transformation

© 2012 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Słowa kluczowe
calcium oxide, pyrolysis, specific surface area, phase transformation