Calcination temperature is a crucial parameter that can be easily controlled to induce a change in material properties. Herein, iron tungstate (FeWO4) was synthesized via a hydrothermal method using iron(II) sulfate heptahydrate and sodium tungstate dihydrate as precursors and calcined at the temperature between 300 oC and 700 oC. With increasing calcination temperature, the saturation magnetization of FeWO4 nanoparticles decreased from 6.6 emu/g for FeWO4 to 0.4 emu/g for FeWO4_700, whereas their band gaps increased from 1.95 eV for FeWO4 to 2.20 eV for FeWO4_700. More crystallinity and crystal defects, and morphological changes at higher calcination temperatures contributed to varying magneto-optical properties of FeWO4 nanoparticles.
</abstract>

Calcination temperature is a crucial parameter that can be easily controlled to induce a change in material properties. Herein, iron tungstate (FeWO4) was synthesized via a hydrothermal method using iron(II) sulfate heptahydrate and sodium tungstate dihydrate as precursors and calcined at the temperature between 300 oC and 700 oC. With increasing calcination temperature, the saturation magnetization of FeWO4 nanoparticles decreased from 6.6 emu/g for FeWO4 to 0.4 emu/g for FeWO4_700, whereas their band gaps increased from 1.95 eV for FeWO4 to 2.20 eV for FeWO4_700. More crystallinity and crystal defects, and morphological changes at higher calcination temperatures contributed to varying magneto-optical properties of FeWO4 nanoparticles.

Effect of calcination temperatures on optical and magnetic properties of FeWO4 nanoparticles

Institute of Applied Technology and Sustainable Development

Polish Journal of Chemical Technology

This work is licensed under the Creative Commons Attribution 4.0 International License.

Effect of calcination temperatures on optical and magnetic properties of FeWO nanoparticles

Calcination temperature is a crucial parameter that can be easily controlled to induce a change in material properties. Herein, iron tungstate (FeWO4) was...

Effect of calcination temperatures on optical and magnetic properties of FeWO₄ nanoparticles

Data publikacji: 03 kwi 2024

Zakres stron: 16 - 23

DOI: https://doi.org/10.2478/pjct-2024-0003

Słowa kluczowe
Iron tungstate, Calcination temperature, Optical, Magnetic, Hydrothermal synthesis

© 2024 Anh Q.K. Nguyen et al., published by Sciendo

This work is licensed under the Creative Commons Attribution 4.0 International License.

Effect of calcination temperatures on optical and magnetic properties of FeWO4 nanoparticles

Data publikacji: 03 kwi 2024

Zakres stron: 16 - 23

DOI: https://doi.org/10.2478/pjct-2024-0003

Słowa kluczoweIron tungstate, Calcination temperature, Optical, Magnetic, Hydrothermal synthesis

© 2024 Anh Q.K. Nguyen et al., published by Sciendo

This work is licensed under the Creative Commons Attribution 4.0 International License.

Effect of calcination temperatures on optical and magnetic properties of FeWO₄ nanoparticles

Słowa kluczowe
Iron tungstate, Calcination temperature, Optical, Magnetic, Hydrothermal synthesis