<abstract xmlns="http://www.w3.org/1999/xhtml"><p>ZnO-CuO flower-like hetero-nanostructures were successfully prepared by combining hydrothermal and dip coating methods. Flower-like hetero-nanostructures of ZnO-CuO were examined by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and UV-Vis. The sensing properties of ZnO-CuO flower-like hetero-nanostructures to volatile organic compounds (VOCs) were evaluated in a chamber containing acetone or isopropanol gas at room temperature. The sensitivity of ZnO-CuO flower-like hetero-nanostructures to VOCs was enhanced compared to that of pure leafage-like ZnO nanostructures. Response and recovery times were about 5 s and 6 s to 50 ppm acetone, and 10 s and 8 s to 50 ppm isopropanol, respectively. The sensing performance of ZnO-CuO flower-like hetero-nanostructures was attributed to the addition of CuO that led to formation of p-n junctions at the interface between the CuO and ZnO. In addition, the sensing mechanism was briefly discussed.</p></abstract>

ZnO-CuO flower-like hetero-nanostructures were successfully prepared by combining hydrothermal and dip coating methods. Flower-like hetero-nanostructures of ZnO-CuO were examined by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), and UV-Vis. The sensing properties of ZnO-CuO flower-like hetero-nanostructures to volatile organic compounds (VOCs) were evaluated in a chamber containing acetone or isopropanol gas at room temperature. The sensitivity of ZnO-CuO flower-like hetero-nanostructures to VOCs was enhanced compared to that of pure leafage-like ZnO nanostructures. Response and recovery times were about 5 s and 6 s to 50 ppm acetone, and 10 s and 8 s to 50 ppm isopropanol, respectively. The sensing performance of ZnO-CuO flower-like hetero-nanostructures was attributed to the addition of CuO that led to formation of p-n junctions at the interface between the CuO and ZnO. In addition, the sensing mechanism was briefly discussed.

Synthesis of ZnO-CuO flower-like hetero-nanostructures as volatile organic compounds (VOCs) sensor at room temperature

Department of Physics, College of Science

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

ZnO-CuO flower-like hetero-nanostructures were successfully prepared by combining hydrothermal and dip coating methods. Flower-like hetero-nanostructures of...

Synthesis of ZnO-CuO flower-like hetero-nanostructures as volatile organic compounds (VOCs) sensor at room temperature

Data publikacji: 02 lis 2018

Zakres stron: 452 - 459

Otrzymano: 19 lip 2017

Przyjęty: 02 maj 2018

DOI: https://doi.org/10.2478/msp-2018-0055

Słowa kluczowe
hydrothermal process, dip coating, hetero-nanostructures, volatile organic compounds (VOCs)

© 2018 Raad S. Sabry et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Synthesis of ZnO-CuO flower-like hetero-nanostructures as volatile organic compounds (VOCs) sensor at room temperature

Data publikacji: 02 lis 2018

Zakres stron: 452 - 459

Otrzymano: 19 lip 2017

Przyjęty: 02 maj 2018

DOI: https://doi.org/10.2478/msp-2018-0055

Słowa kluczowehydrothermal process, dip coating, hetero-nanostructures, volatile organic compounds (VOCs)

© 2018 Raad S. Sabry et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Słowa kluczowe
hydrothermal process, dip coating, hetero-nanostructures, volatile organic compounds (VOCs)