<abstract xmlns="http://www.w3.org/1999/xhtml">
<p>Galvanised steel serves as a base material for pipelines in fire protection systems. However, this system is known for its occasional corrosion failures. The Systems with residual water and oxygen access contribute to formation of macrocells due to different aeration, which can lead to severe damage of the pipes. The aim of this work was to investigate the cause of localized corrosion on the galvanised pipes designated for the fire protection system. The results proved that the main cause of the fire protection pipe system was the residual water in the pipe. The influence of differential aeration on the corrosion of zinc and steel was studied by resistometric technique and showed no effect on the failure of material.</p>
</abstract>

Galvanised steel serves as a base material for pipelines in fire protection systems. However, this system is known for its occasional corrosion failures. The Systems with residual water and oxygen access contribute to formation of macrocells due to different aeration, which can lead to severe damage of the pipes. The aim of this work was to investigate the cause of localized corrosion on the galvanised pipes designated for the fire protection system. The results proved that the main cause of the fire protection pipe system was the residual water in the pipe. The influence of differential aeration on the corrosion of zinc and steel was studied by resistometric technique and showed no effect on the failure of material.

Localized corrosion attack on the galvanised steel pipes of the fire protection system

Institute of Inorganic Technologies and Materials

Department of Metals and Corrosion Engineering

University of Chemistry and Technology Prague

Koroze a ochrana materiálu

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Galvanised steel serves as a base material for pipelines in fire protection systems. However, this system is known for its occasional corrosion failures. The...

Localized corrosion attack on the galvanised steel pipes of the fire protection system

Data publikacji: 04 kwi 2024

Zakres stron: 28 - 42

DOI: https://doi.org/10.2478/kom-2024-0004

© 2024 R. Košťúr et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.