<p>This paper is focused on the problematics of weld joint corrosive degradation in the boiler water environment. The boiler water is commonly used in power industry. The corrosion experiment simulated the boiler water environment during shutdown, when chemicals may be concentrated in the deposits, or as a result of evaporation. The corrosion experiment was performed on heterogeneous weldments made of P265GH//X6CrNiTi18-9 steels in the environment of stagnant boiler water with the addition of NaCl for 53 days. The data showed only minimal weight losses, and small changes in the measured fracture toughness of the welded joint. At the same time, a tendency for a mechanical weakening of the welded joint with the increasing aggressivity of the boiler water environment was observed. The metallographic analysis was performed to describe the nature of corrosive degradation.</p>
</abstract>

This paper is focused on the problematics of weld joint corrosive degradation in the boiler water environment. The boiler water is commonly used in power industry. The corrosion experiment simulated the boiler water environment during shutdown, when chemicals may be concentrated in the deposits, or as a result of evaporation. The corrosion experiment was performed on heterogeneous weldments made of P265GH//X6CrNiTi18-9 steels in the environment of stagnant boiler water with the addition of NaCl for 53 days. The data showed only minimal weight losses, and small changes in the measured fracture toughness of the welded joint. At the same time, a tendency for a mechanical weakening of the welded joint with the increasing aggressivity of the boiler water environment was observed. The metallographic analysis was performed to describe the nature of corrosive degradation.

Dissimilar weld joint corrosion in simulated boiler water environment

KOM – Corrosion and Material Protection Journal

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

{"article-title":"Dissimilar weld joint corrosion in simulated boiler water environment"}

This paper is focused on the problematics of weld joint corrosive degradation in the boiler water environment. The boiler water is commonly used in power...

Dissimilar weld joint corrosion in simulated boiler water environment

Data publikacji: 18 kwi 2022

Zakres stron: 16 - 19

DOI: https://doi.org/10.2478/kom-2022-0003

© 2022 J. Hodač et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.