Chemical resistance of NR/SBR rubber blends for surfaces corrosion protection of metallic tanks in petrochemical industries

In this work, a series of Natural Rubber (NR)/Styrene Butadiene Rubber (SBR) blends were formulated to protect metallic petrochemical storage tanks from corrosive media. Therefore, these blends tested against a 10% HCl solution for 72 hr at room temperature. Blends series were prepared with different ratios of NR/SBR; 25/75, 30/70, 35/65, 40/60, 45/55, 50/50, and 55/45. Three types of carbon black (N-330, N-660, and N-762) were added individually to the 45/55 blend. Hardness, tensile strength, modulus, and elongation properties were tested before and after immersion in the 10% HCl attack media. All these mechanical properties decreased after immersion action accept hardness property. Up to 45 phr NR content, the hardness increased linearly independent on immersion action, but HCl immersion gives higher hardness values. Tensile strength increased up to 40 phr NR content with and without immersion and the immersion action decreased tensile values. The highest elongation value obtained with 35/65 blend with and without immersion. The 45 phr NR content gives the higher modulus, while the lowest value obtained with the 30 phhr content. For 45/55 blend, the hardness increased as the carbon black particle size decreased and immersion action gives higher hardness values. The tensile strength decreased linearly with the carbon black surface area, while with the medium surface area, the highest modulus and lowest elongation obtained.