<abstract xmlns="http://www.w3.org/1999/xhtml">The coating prepared by plasma electrolytic oxidation (PEO) was created on AZ31 magnesium alloy surface with the aim to evaluate its effect on corrosion resistance. The DC current was applied on the sample in solution consisted of 10 g/l Na3PO4·12H2O and 1 g/l KOH. Additional samples were prepared with 2 and 4 minutes of preparation to observe evolution of the PEO coating. Morphology of the coatings was evaluated by scanning electron microscopy and chemical composition was examined by EDX analysis. Electrochemical characteristic were measured by potentiodynamic polarization tests and electrochemical impedance spectroscopy in 0.1 M NaCl at the laboratory temperature. Obtained data were presented in form of potentiodynamic curves and Nyquist diagrams. Results of analysis showed that plasma electrolytic oxidation coating positively influence corrosion resistance of AZ31 magnesium alloy in chosen corrosive environment.</abstract>

The coating prepared by plasma electrolytic oxidation (PEO) was created on AZ31 magnesium alloy surface with the aim to evaluate its effect on corrosion resistance. The DC current was applied on the sample in solution consisted of 10 g/l Na3PO4·12H2O and 1 g/l KOH. Additional samples were prepared with 2 and 4 minutes of preparation to observe evolution of the PEO coating. Morphology of the coatings was evaluated by scanning electron microscopy and chemical composition was examined by EDX analysis. Electrochemical characteristic were measured by potentiodynamic polarization tests and electrochemical impedance spectroscopy in 0.1 M NaCl at the laboratory temperature. Obtained data were presented in form of potentiodynamic curves and Nyquist diagrams. Results of analysis showed that plasma electrolytic oxidation coating positively influence corrosion resistance of AZ31 magnesium alloy in chosen corrosive environment.

Corrosion resistance of AZ31 magnesium alloy treated by plasma electrolytic oxidation

Strojnícka fakulta, Katedra materiálového inžinierstva

Vysoké učení technické v Brně, Fakulta chemická

Koroze a ochrana materiálu

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The coating prepared by plasma electrolytic oxidation (PEO) was created on AZ31 magnesium alloy surface with the aim to evaluate its effect on corrosion...

Corrosion resistance of AZ31 magnesium alloy treated by plasma electrolytic oxidation

Data publikacji: 26 cze 2019

Zakres stron: 65 - 71

DOI: https://doi.org/10.2478/kom-2019-0008

© 2019 D. Kajánek et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.