<abstract xmlns="http://www.w3.org/1999/xhtml">Samarium niobate SmNbO4 (SNO) and tantalate SmTaO4 (STO) thin films (~100 nm) were prepared by sol-gel/spin-coating process on alumina substrates with PZT interlayer and annealing at 1000°C. The precursors of films were synthesized using Nb or Ta tartrate complexes. The improvement of the crystallinity of monoclinic M′-SmTaO4 phase via heating was observed through the coexistence of small amounts of tetragonal T-SmTa7O19 phase in STO precursor at 1000°C. The XRD results of SNO and STO films confirmed monoclinic M-SmNbO4 and M′-SmTaO4 phases, respectively, with traces of orthorhombic O-SmNbO4 (in SNO). In STO film, the single monoclinic M′-SmTaO4 phase was revealed. The surface morphology and topography of thin films were investigated by SEM and AFM analysis. STO film was smoother with roughness 3.2 nm in comparison with SNO (6.3 nm). In the microstructure of SNO film, small spherical (~50 nm) and larger cuboidal particles (~100 nm) of the SmNbO4 phase were observed. In STO, compact clusters composed of fine spherical SmTaO4 particles (~20-50 nm) were found. Effect of samarium can contribute to the formation different polymorphs of these films for the application to environmental electrolytic thin film devices.</abstract>

Samarium niobate SmNbO4 (SNO) and tantalate SmTaO4 (STO) thin films (~100 nm) were prepared by sol-gel/spin-coating process on alumina substrates with PZT interlayer and annealing at 1000°C. The precursors of films were synthesized using Nb or Ta tartrate complexes. The improvement of the crystallinity of monoclinic M′-SmTaO4 phase via heating was observed through the coexistence of small amounts of tetragonal T-SmTa7O19 phase in STO precursor at 1000°C. The XRD results of SNO and STO films confirmed monoclinic M-SmNbO4 and M′-SmTaO4 phases, respectively, with traces of orthorhombic O-SmNbO4 (in SNO). In STO film, the single monoclinic M′-SmTaO4 phase was revealed. The surface morphology and topography of thin films were investigated by SEM and AFM analysis. STO film was smoother with roughness 3.2 nm in comparison with SNO (6.3 nm). In the microstructure of SNO film, small spherical (~50 nm) and larger cuboidal particles (~100 nm) of the SmNbO4 phase were observed. In STO, compact clusters composed of fine spherical SmTaO4 particles (~20-50 nm) were found. Effect of samarium can contribute to the formation different polymorphs of these films for the application to environmental electrolytic thin film devices.

Phase Composition of Samarium Niobate and Tantalate Thin Films Prepared by Sol-Gel Method

Powder Metallurgy Progress

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Samarium niobate SmNbO4 (SNO) and tantalate SmTaO4 (STO) thin films (~100 nm) were prepared by sol-gel/spin-coating process on alumina substrates with PZT...

Phase Composition of Samarium Niobate and Tantalate Thin Films Prepared by Sol-Gel Method

Data publikacji: 21 gru 2017

Zakres stron: 10 - 20

DOI: https://doi.org/10.1515/pmp-2017-0002

Słowa kluczowe
sol-gel, thin films, SmNbO, SmTaO, monoclinic phase, microstructure

© 2017 H. Bruncková et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Phase Composition of Samarium Niobate and Tantalate Thin Films Prepared by Sol-Gel Method

Data publikacji: 21 gru 2017

Zakres stron: 10 - 20

DOI: https://doi.org/10.1515/pmp-2017-0002

Słowa kluczowesol-gel, thin films, SmNbO, SmTaO, monoclinic phase, microstructure

© 2017 H. Bruncková et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Słowa kluczowe
sol-gel, thin films, SmNbO, SmTaO, monoclinic phase, microstructure