<abstract xmlns="http://www.w3.org/1999/xhtml">During the last decades, thermally modified wood has become an object of interest among the wood scientists as an environmentally friendly material, because nowadays environmental aspects of materials have become more and more significant. Leaching is one of the processes that occurs in outdoor use. The aim of this study was to evaluate concentration of potentially hazardous substances in leachates of thermally modified pine wood. Scots pine (<italic>Pinus sylvestris</italic> L.) wood was thermally modified using Wood Treatment Technology (WTT) company device at 170 °C for 1 hour (TMP170/1) and at 160 °C for 3 hours (TMP160/3) and the mass loss was calculated. Material preparation and leaching procedure was made according to standard LVS EN 84:2000. In obtained leachates, the content of sugars, acetic acid, furfural and tannic acid were determined. Results showed that the total wood mass loss was 7.1 ± 1.4% (n=20) for TMP170/1 and 4.0 ± 1.6% (n=20) for TMP160/3. The initial leaching velocity differs between both modes and is higher for TMP160/3. The velocity decreases exponentially with immersion time and reaches plateau after 7th (5 days) immersion, but leaching still continues after the 9th immersion (14 days). The main components in leachates were tannic acid and pentoses. Among all studied compounds furfural is the hardest leachable one. Thermally modified wood treated at TMP170/1 is more environmentally friendly due to less water leachable substances. It is worth looking forward by investigating volatile organic compounds emissions in the air as it also could give high impact on human health.</abstract>

During the last decades, thermally modified wood has become an object of interest among the wood scientists as an environmentally friendly material, because nowadays environmental aspects of materials have become more and more significant. Leaching is one of the processes that occurs in outdoor use. The aim of this study was to evaluate concentration of potentially hazardous substances in leachates of thermally modified pine wood. Scots pine (Pinus sylvestris L.) wood was thermally modified using Wood Treatment Technology (WTT) company device at 170 °C for 1 hour (TMP170/1) and at 160 °C for 3 hours (TMP160/3) and the mass loss was calculated. Material preparation and leaching procedure was made according to standard LVS EN 84:2000. In obtained leachates, the content of sugars, acetic acid, furfural and tannic acid were determined. Results showed that the total wood mass loss was 7.1 ± 1.4% (n=20) for TMP170/1 and 4.0 ± 1.6% (n=20) for TMP160/3. The initial leaching velocity differs between both modes and is higher for TMP160/3. The velocity decreases exponentially with immersion time and reaches plateau after 7th (5 days) immersion, but leaching still continues after the 9th immersion (14 days). The main components in leachates were tannic acid and pentoses. Among all studied compounds furfural is the hardest leachable one. Thermally modified wood treated at TMP170/1 is more environmentally friendly due to less water leachable substances. It is worth looking forward by investigating volatile organic compounds emissions in the air as it also could give high impact on human health.

Leachates of Thermally Modified Pine (<italic>Pinus sylvestris</italic> L.) Wood

Latvian State Institute of Wood Chemistry, Dzērbenes str. 27, LV-1006, Latvia

Rural Sustainability Research

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Leachates of Thermally Modified Pine ( L.) Wood

During the last decades, thermally modified wood has become an object of interest among the wood scientists as an environmentally friendly material, because...

Leachates of Thermally Modified Pine (Pinus sylvestris L.) Wood

Data publikacji: 19 sty 2016

Zakres stron: 26 - 31

DOI: https://doi.org/10.1515/plua-2015-0010

Słowa kluczowe
Thermally modified wood, leachates, furfural, softwood

© 2015 Anete Meija-Feldmane, published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Leachates of Thermally Modified Pine (Pinus sylvestris L.) Wood

Data publikacji: 19 sty 2016

Zakres stron: 26 - 31

DOI: https://doi.org/10.1515/plua-2015-0010

Słowa kluczoweThermally modified wood, leachates, furfural, softwood

© 2015 Anete Meija-Feldmane, published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Słowa kluczowe
Thermally modified wood, leachates, furfural, softwood