<abstract xmlns="http://www.w3.org/1999/xhtml"><p>The elastomeric anti-trauma pad (EA-TP) based on shear thickening fluid (STF) has been developed. Dynamic oscillatory shear experiment was conducted at constant strain amplitude of 5%. STF composed of 25% of volume fraction of 7 nm Fumed Silica, dispersed in polypropylene glycol with molar mass 400 gmol<sup>−1</sup> shows elastic properties in entire investigated range of the frequency. Ballistic tests of EA-TP with 7.62 mm × 39 mm PS bullets were performed according to the PN-V-87000:2011 standard. The studies revealed about 60% reduction of the average backface signature depth (BSD) for the EA-TP, when compared to the nowadays commonly used soft insert. The ATR-FTIR analysis confirmed slight impact of the elevated temperature and air (oxygen) on the chemical degradation of the EA-TP surface. The UV-VIS spectroscopy has allowed to notice colour deviation of the aged samples towards green and yellow, as well as lack of dye resistance to accelerated aging process. Thermographic analysis has shown no visible changes of the EA-TP surface and sub-surface during accelerated aging process. The aforementioned small changes on the surface of EA-TP did not affect the ballistic properties of composite armour. EA-TP insert maintains ballistic properties after accelerated aging process which was simulating the period of 6 years according to ASTM F1980 – 07:2002 standard.</p></abstract>

The elastomeric anti-trauma pad (EA-TP) based on shear thickening fluid (STF) has been developed. Dynamic oscillatory shear experiment was conducted at constant strain amplitude of 5%. STF composed of 25% of volume fraction of 7 nm Fumed Silica, dispersed in polypropylene glycol with molar mass 400 gmol−1 shows elastic properties in entire investigated range of the frequency. Ballistic tests of EA-TP with 7.62 mm × 39 mm PS bullets were performed according to the PN-V-87000:2011 standard. The studies revealed about 60% reduction of the average backface signature depth (BSD) for the EA-TP, when compared to the nowadays commonly used soft insert. The ATR-FTIR analysis confirmed slight impact of the elevated temperature and air (oxygen) on the chemical degradation of the EA-TP surface. The UV-VIS spectroscopy has allowed to notice colour deviation of the aged samples towards green and yellow, as well as lack of dye resistance to accelerated aging process. Thermographic analysis has shown no visible changes of the EA-TP surface and sub-surface during accelerated aging process. The aforementioned small changes on the surface of EA-TP did not affect the ballistic properties of composite armour. EA-TP insert maintains ballistic properties after accelerated aging process which was simulating the period of 6 years according to ASTM F1980 – 07:2002 standard.

Thermal stability of the elastomeric anti-trauma pad

Institute of Security Technologies “MORATEX”

Faculty of Materials Science and Engineering

Polish Journal of Chemical Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Thermal stability of the elastomeric anti-trauma pad"}

The elastomeric anti-trauma pad (EA-TP) based on shear thickening fluid (STF) has been developed. Dynamic oscillatory shear experiment was conducted at...

Thermal stability of the elastomeric anti-trauma pad

Data publikacji: 08 lip 2017

Zakres stron: 93 - 100

DOI: https://doi.org/10.1515/pjct-2017-0034

Słowa kluczowe
anti-trauma pad, shear thickening fluid, accelerated aging

© 2017 Karolina Olszewska et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Thermal stability of the elastomeric anti-trauma pad

Data publikacji: 08 lip 2017

Zakres stron: 93 - 100

DOI: https://doi.org/10.1515/pjct-2017-0034

Słowa kluczoweanti-trauma pad, shear thickening fluid, accelerated aging

© 2017 Karolina Olszewska et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Słowa kluczowe
anti-trauma pad, shear thickening fluid, accelerated aging