Some observations on the synthesis and electrolytic properties of (Ba1-xCax) (M0.9Y0.1)O3, M = Ce, Zr-based samples modified with calcium

Magdalena Dudek

Magdalena Dudek

Poland
Wyszukaj tego autora
Sciendo|Google Scholar
Dudek, Magdalena
, 
Bartłomiej Lis

Bartłomiej Lis

Poland
Wyszukaj tego autora
Sciendo|Google Scholar
Lis, Bartłomiej
, 
Alicja Rapacz-Kmita

Alicja Rapacz-Kmita

Poland
Wyszukaj tego autora
Sciendo|Google Scholar
Rapacz-Kmita, Alicja
, 
Marcin Gajek

Marcin Gajek

Poland
Wyszukaj tego autora
Sciendo|Google Scholar
Gajek, Marcin
, 
Andrzej Raźniak

Andrzej Raźniak

Poland
Wyszukaj tego autora
Sciendo|Google Scholar
Raźniak, Andrzej
 oraz 
Ewa Drożdż

Ewa Drożdż

Poland
Wyszukaj tego autora
Sciendo|Google Scholar
Drożdż, Ewa
  
27 kwi 2016
Some observations on the synthesis and electrolytic properties of (Ba1-xCax) (M0.9Y0.1)O3, M = Ce, Zr-based samples modified with calcium's Cover Image
O artykule
Poprzedni artykuł
Następny artykuł
Zacytuj
Pobierz okładkę
Kategoria artykułu: Research Article
Data publikacji: 27 kwi 2016
Zakres stron: 101 - 114
Otrzymano: 07 lip 2015
Przyjęty: 11 gru 2015
DOI: https://doi.org/10.1515/msp-2016-0022
Słowa kluczowe
© 2016 Wroclaw University of Technology
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Fig. 1

a) DTA and TG curves recorded for dried BaCe0.9Y0.1O3 and Ba0.95Ca0.05Ce0.9Y0.1O3 precursors; b) EGA gas analysis performed during DTA/TG thermal studies.
a) DTA and TG curves recorded for dried BaCe0.9Y0.1O3 and Ba0.95Ca0.05Ce0.9Y0.1O3 precursors; b) EGA gas analysis performed during DTA/TG thermal studies.

Fig. 2

Evolution of the X-ray diffraction pattern for theBaCe0.9Y0.1O3dried precursor.
Evolution of the X-ray diffraction pattern for theBaCe0.9Y0.1O3dried precursor.

Fig. 3

Variations in cell volume vs. chemical compositionof the (Ba1-xCax)(M0.9Y0.1), M = Ce, Zrsintered samples series.
Variations in cell volume vs. chemical compositionof the (Ba1-xCax)(M0.9Y0.1), M = Ce, Zrsintered samples series.

Fig. 4

Representative TEM microscopy imagesrecorded for: Ba0.95Ca0.05Zr0.9Y0.1O3 (a) and Ba0.95Ca0.05Ce0.9Y0.1O3 (b) powders.
Representative TEM microscopy imagesrecorded for: Ba0.95Ca0.05Zr0.9Y0.1O3 (a) and Ba0.95Ca0.05Ce0.9Y0.1O3 (b) powders.

Fig. 5

Dilatometric curves recorded for pellets during non-isothermalconditions between 25 and 1300 °C.
Dilatometric curves recorded for pellets during non-isothermalconditions between 25 and 1300 °C.

Fig. 6

SEM microphotographs of the microstructureof sintered samples: (a) BaZr0.9Y0.1O3, (b) Ba0.95Ca0.05Zr0.9Y0.1O3, and (c) Ba0.95Ca0.1 (Ce0.9Y0.1) O3.
SEM microphotographs of the microstructureof sintered samples: (a) BaZr0.9Y0.1O3, (b) Ba0.95Ca0.05Zr0.9Y0.1O3, and (c) Ba0.95Ca0.1 (Ce0.9Y0.1) O3.

Fig. 7

The temperature dependence of total electrical conductivity of (Ba1-xCax) (M0.9Y0.1) O3 M =Ce, Zr sintered samples measured in dry air.
The temperature dependence of total electrical conductivity of (Ba1-xCax) (M0.9Y0.1) O3 M =Ce, Zr sintered samples measured in dry air.

Fig. 8

The family of I-t curves recorded at 700 °C at overpotential (∆E −0.05 to −0.5 V). The Ba0.9Ca0.1Ce0.9Y0.1O3 electrolyte was used in this measurement.
The family of I-t curves recorded at 700 °C at overpotential (∆E −0.05 to −0.5 V). The Ba0.9Ca0.1Ce0.9Y0.1O3 electrolyte was used in this measurement.

Fig. 9

The family of I-t curves recorded at 700 °C under ∆E = −0.5 V in different gas atmospheres. The BaZr0.9Y0.1O3 electrolyte was used in this investigation.
The family of I-t curves recorded at 700 °C under ∆E = −0.5 V in different gas atmospheres. The BaZr0.9Y0.1O3 electrolyte was used in this investigation.

Fig. 10

The Nyquist plots for the Pt|BZY system recorded before and after polarization ∆E =-0.5 V. The measurements were performed at 700 °C in a wet argon gas atmosphere.
The Nyquist plots for the Pt|BZY system recorded before and after polarization ∆E =-0.5 V. The measurements were performed at 700 °C in a wet argon gas atmosphere.

Fig. 11

SEM images of Pt deposit on the surface of the BZY electrolyte recorded after polarization experiments.
SEM images of Pt deposit on the surface of the BZY electrolyte recorded after polarization experiments.

Fig. 12

The temperature dependence of OCV on the cells: O2|Pt|BCY and 5CBCY|Pt|H2 recorded between 500 to 850 °C.
The temperature dependence of OCV on the cells: O2|Pt|BCY and 5CBCY|Pt|H2 recorded between 500 to 850 °C.

Fig.13

The family curves U-I and P-I recorded for the cell: H2|Pt|BZY and 5CBZY|Pt|O2 at 850 °C.
The family curves U-I and P-I recorded for the cell: H2|Pt|BZY and 5CBZY|Pt|O2 at 850 °C.

The total electrical conductivity σ (S/cm) andactivation energy calculated in the temperature range of 300 to 700 °C_ Data of measurements in wet 5 % H2 in Ar_

Materialσ [S/cm] at 600 °CEa [eV]
BaZr0.9Y0.1O38.29 × 10–40.78
Ba0.95Ca0.05Zr0.9Y0.1O31.24 × 10–30.74
Ba0.9Ca0.1Zr0.9Y0.1O39.05 × 10–40.80
BaCe0.9Y0.1O31.16 × 10–30.64
Ba0.95Ca0.05Ce0.9Y0.1O38.21 × 10–30.53
Ba0.9Ca0.1Ce0.9Y0.1O34.11 × 10–30.57

Hardness HV and fracture toughness KIc of selected (Ba1-xCax) (M0_9Y0_1) O3, M = Zr, Ce_

MaterialHV, GPaKICMPa·m0.5
BaZr0.9Y0.1O38.11±0.212.35±0.23
Ba0.95Ca0.05Zr0.9Y0.1O38.36±0.192.42±0.17
Ba0.9Ca0.1Zr0.9Y0.1O38.16±0.272.28±0.18
BaCe0.9Y0.1O37.01±0.181.66±0.24
Ba0.95Ca0.05Ce0.9Y0.1O37.19±0.111.74±0.22
Ba0.9Ca0.1Ce0.9Y0.1O37.24±0.201.88±0.28