<abstract xmlns="http://www.w3.org/1999/xhtml">Dielectric ceramics samples of barium titanium oxide doped with samarium, having a complex structural formula of Ba2-xSm4+2x/3Ti8O24 (referred to as BST), were fabricated by a high temperature solid-state reaction technique with varying x (0.0, 0.2, 0.4, 0.6). X-ray diffraction technique was used to check the formation of particular phases. Scanning electron microscope technique was used to study the surface morphology of the samples. The samples were studied in a temperature range of 298 K to 623 K and frequency range of 10 KHz to 1 MHz. The dielectric constant (εr), loss tangent (tan δ), and AC conductivity (σAC) were measured on sintered disks of BST samples. The DC resistivity of different compositions was measured at room temperature. Detailed studies of dielectric and electrical properties showed that these properties are strongly dependent on composition, frequency and temperature. The compounds showed stable behavior in lower temperature range (up to 523 K), therefore, they can be used in practical applications in this temperature range. </abstract>

Dielectric ceramics samples of barium titanium oxide doped with samarium, having a complex structural formula of Ba2-xSm4+2x/3Ti8O24 (referred to as BST), were fabricated by a high temperature solid-state reaction technique with varying x (0.0, 0.2, 0.4, 0.6). X-ray diffraction technique was used to check the formation of particular phases. Scanning electron microscope technique was used to study the surface morphology of the samples. The samples were studied in a temperature range of 298 K to 623 K and frequency range of 10 KHz to 1 MHz. The dielectric constant (εr), loss tangent (tan δ), and AC conductivity (σAC) were measured on sintered disks of BST samples. The DC resistivity of different compositions was measured at room temperature. Detailed studies of dielectric and electrical properties showed that these properties are strongly dependent on composition, frequency and temperature. The compounds showed stable behavior in lower temperature range (up to 523 K), therefore, they can be used in practical applications in this temperature range.

Frequency and temperature dependence of dielectric and electric properties of Ba2-xSm4+2x/3Ti8O24 with structural analysis

Department of Electronics Technology, Guru Nanak Dev University, Amritsar, Punjab, India

Department of Electronics and Communication Engineering, Punjab Technical University, PIT University Campus, Kapurthala, India

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Frequency and temperature dependence of dielectric and electric properties of BaSmTiO with structural analysis

Dielectric ceramics samples of barium titanium oxide doped with samarium, having a complex structural formula of Ba2-xSm4+2x/3Ti8O24 (referred to as BST), were...

Frequency and temperature dependence of dielectric and electric properties of Ba_2-xSm_4+2x/3Ti₈O₂₄ with structural analysis

Data publikacji: 11 lip 2015

Zakres stron: 268 - 277

Otrzymano: 02 maj 2014

Przyjęty: 09 sty 2015

DOI: https://doi.org/10.1515/msp-2015-0034

© 2015

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.