<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml">Polyvinyl acetate (PVAc) loaded Bi2O3 nano-particles were successfully prepared at room temperature and ambient pressure. Transmission electron microscopy was used to characterize the final product. It was found that Bi2O3 nanoparticles were well dispersed and uniform in shape and the diameter of the particles was confined within 8 nm. Addition of small amounts (0.2 - 1 wt%) of nano-scales Bismuth oxide (Bi2O3) to polyvinyl acetate (PVAc) are increased the electrical conductivity as well as the modulus of elasticity. The deformation behavior after yielding of the nanocomposites, irrespective of Bi2O3 concentration is similar to the unfilled elastomer, implying that the mechanism of large deformation is mainly governed by the matrix.</abstract>

Polyvinyl acetate (PVAc) loaded Bi2O3 nano-particles were successfully prepared at room temperature and ambient pressure. Transmission electron microscopy was used to characterize the final product. It was found that Bi2O3 nanoparticles were well dispersed and uniform in shape and the diameter of the particles was confined within 8 nm. Addition of small amounts (0.2 - 1 wt%) of nano-scales Bismuth oxide (Bi2O3) to polyvinyl acetate (PVAc) are increased the electrical conductivity as well as the modulus of elasticity. The deformation behavior after yielding of the nanocomposites, irrespective of Bi2O3 concentration is similar to the unfilled elastomer, implying that the mechanism of large deformation is mainly governed by the matrix.

The Effect of Nanoscale Bismuth Oxide on the Electrical and Mechanical Properties of Polyvinyl Acetate

Chemistry Department, Faculty of Science, King AbdulAziz University, P.O.Box.80203, Jeddah 21589, Saudi Arabia

Chemistry Department, Faculty of Science, Benha University, Benha, Egypt

Physics Department, Faculty of Science, King AbdulAziz University

Physics Department, Faculty of Science, Suez Canal University, Ismaillia, Egypt

Advances in Materials Science

Polyvinyl acetate (PVAc) loaded Bi2O3 nano-particles were successfully prepared at room temperature and ambient pressure. Transmission electron microscopy was...

The Effect of Nanoscale Bismuth Oxide on the Electrical and Mechanical Properties of Polyvinyl Acetate

Pubblicato online: 17 lug 2009

Pagine: 14 - 22

DOI: https://doi.org/10.2478/v10077-009-0002-4

This content is open access.