Analysis of the effect of curing and mixing periods on mechanical properties of the geopolymer composite

Manvendra Verma

Manvendra Verma

Department of Civil Engineering, GLA UniversityMathura, India
Cerca questo autore su
Sciendo|Google Scholar
Verma, Manvendra
, 
Rahul Kumar Meena

Rahul Kumar Meena

Department of Civil Engineering, NITDelhi, India
Cerca questo autore su
Sciendo|Google Scholar
Meena, Rahul Kumar
, 
Mohammad Iqbal Khan

Mohammad Iqbal Khan

Civil Engineering, College of Engineering, King Saud UniversityRiyadh, Saudi Arabia
Cerca questo autore su
Sciendo|Google Scholar
Khan, Mohammad Iqbal
 e 
Jamal M. Khatib

Jamal M. Khatib

Faculty of Science and Engineering, University of WolverhamptonWolverhampton, United Kingdom
Cerca questo autore su
Sciendo|Google Scholar
Khatib, Jamal M.
  
31 dic 2024
Analysis of the effect of curing and mixing periods on mechanical properties of the geopolymer composite's Cover Image
INFORMAZIONI SU QUESTO ARTICOLO
Articolo precedente
Articolo Successivo
Cita
Scarica la copertina
Categoria dell'articolo: Research Article
Pubblicato online: 31 dic 2024
Pagine: 131 - 147
Ricevuto: 16 mag 2024
Accettato: 09 gen 2025
DOI: https://doi.org/10.2478/msp-2024-0050
Parole chiave
© 2024 the Manvendra Verma et al., published by Sciendo
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Figure 1

Picture of XRD analysis of fly ash and GGBFS.
Picture of XRD analysis of fly ash and GGBFS.

Figure 2

(a) Fly ash SEM image and (b) GGBFS SEM image.
(a) Fly ash SEM image and (b) GGBFS SEM image.

Figure 3

(a) Gradation curves of coarse and fine aggregates and (b) picture during mixing.
(a) Gradation curves of coarse and fine aggregates and (b) picture during mixing.

Figure 4

(a) Picture of oven-curing of specimens, (b) slump value variation with the mixing time, (c) setting time variation with the mixing time, (d) density variation with the mixing time, and (e) drying shrinkage variation with the mixing time.
(a) Picture of oven-curing of specimens, (b) slump value variation with the mixing time, (c) setting time variation with the mixing time, (d) density variation with the mixing time, and (e) drying shrinkage variation with the mixing time.

Figure 5

(a) Compressive strength of GPC mix, (b) splitting tensile strength variation of GPC, (c) flexural strength variation with mixing time, (d) picture of elastic modulus finding setup, and (e) graph of elastic modulus variation with mixing time.
(a) Compressive strength of GPC mix, (b) splitting tensile strength variation of GPC, (c) flexural strength variation with mixing time, (d) picture of elastic modulus finding setup, and (e) graph of elastic modulus variation with mixing time.

Figure 6

(a) Rebound strength variation with the mixing time and (b) UPV variations with the mixing time.
(a) Rebound strength variation with the mixing time and (b) UPV variations with the mixing time.

Figure 7

(a) Density and elastic modulus variation with the curing time, (b) graph between the curing period and drying shrinkage, (c) compressive strength variation with the curing time, (d) splitting tensile variation with the curing period, and (e) flexural strength variation with the curing period.
(a) Density and elastic modulus variation with the curing time, (b) graph between the curing period and drying shrinkage, (c) compressive strength variation with the curing time, (d) splitting tensile variation with the curing period, and (e) flexural strength variation with the curing period.

Figure 8

(a) Rebound strength variation with the curing period and (b) UPV variation with the curing period.
(a) Rebound strength variation with the curing period and (b) UPV variation with the curing period.
Lingua:
Inglese
Frequenza di pubblicazione:
4 volte all'anno
Argomenti della rivista:
Scienze materiali, Scienze materiali, altro, Nanomateriali, Materiali funzionali ed intelligenti, Caratteristica e proprietà dei materiali
Feed RSS della rivista