Analysis of the effect of curing and mixing periods on mechanical properties of the geopolymer composite

Manvendra Verma

Manvendra Verma

Department of Civil Engineering, GLA UniversityMathura, India
Buscar este autor en
Sciendo|Google Scholar
Verma, Manvendra
, 
Rahul Kumar Meena

Rahul Kumar Meena

Department of Civil Engineering, NITDelhi, India
Buscar este autor en
Sciendo|Google Scholar
Meena, Rahul Kumar
, 
Mohammad Iqbal Khan

Mohammad Iqbal Khan

Civil Engineering, College of Engineering, King Saud UniversityRiyadh, Saudi Arabia
Buscar este autor en
Sciendo|Google Scholar
Khan, Mohammad Iqbal
 y 
Jamal M. Khatib

Jamal M. Khatib

Faculty of Science and Engineering, University of WolverhamptonWolverhampton, United Kingdom
Buscar este autor en
Sciendo|Google Scholar
Khatib, Jamal M.
  
31 dic 2024
Analysis of the effect of curing and mixing periods on mechanical properties of the geopolymer composite's Cover Image
Acerca de este artículo
Artículo anterior
Artículo siguiente
Cite
Descargar portada
Categoría del artículo: Research Article
Publicado en línea: 31 dic 2024
Páginas: 131 - 147
Recibido: 16 may 2024
Aceptado: 09 ene 2025
DOI: https://doi.org/10.2478/msp-2024-0050
Palabras clave
© 2024 the Manvendra Verma et al., published by Sciendo
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Figure 1

Picture of XRD analysis of fly ash and GGBFS.
Picture of XRD analysis of fly ash and GGBFS.

Figure 2

(a) Fly ash SEM image and (b) GGBFS SEM image.
(a) Fly ash SEM image and (b) GGBFS SEM image.

Figure 3

(a) Gradation curves of coarse and fine aggregates and (b) picture during mixing.
(a) Gradation curves of coarse and fine aggregates and (b) picture during mixing.

Figure 4

(a) Picture of oven-curing of specimens, (b) slump value variation with the mixing time, (c) setting time variation with the mixing time, (d) density variation with the mixing time, and (e) drying shrinkage variation with the mixing time.
(a) Picture of oven-curing of specimens, (b) slump value variation with the mixing time, (c) setting time variation with the mixing time, (d) density variation with the mixing time, and (e) drying shrinkage variation with the mixing time.

Figure 5

(a) Compressive strength of GPC mix, (b) splitting tensile strength variation of GPC, (c) flexural strength variation with mixing time, (d) picture of elastic modulus finding setup, and (e) graph of elastic modulus variation with mixing time.
(a) Compressive strength of GPC mix, (b) splitting tensile strength variation of GPC, (c) flexural strength variation with mixing time, (d) picture of elastic modulus finding setup, and (e) graph of elastic modulus variation with mixing time.

Figure 6

(a) Rebound strength variation with the mixing time and (b) UPV variations with the mixing time.
(a) Rebound strength variation with the mixing time and (b) UPV variations with the mixing time.

Figure 7

(a) Density and elastic modulus variation with the curing time, (b) graph between the curing period and drying shrinkage, (c) compressive strength variation with the curing time, (d) splitting tensile variation with the curing period, and (e) flexural strength variation with the curing period.
(a) Density and elastic modulus variation with the curing time, (b) graph between the curing period and drying shrinkage, (c) compressive strength variation with the curing time, (d) splitting tensile variation with the curing period, and (e) flexural strength variation with the curing period.

Figure 8

(a) Rebound strength variation with the curing period and (b) UPV variation with the curing period.
(a) Rebound strength variation with the curing period and (b) UPV variation with the curing period.
Idioma:
Inglés
Calendario de la edición:
4 veces al año
Temas de la revista:
Ciencia de los materiales, Ciencia de los materiales, otros, Nanomateriales, Materiales funcionales e inteligentes, Características y propiedades de los materiales
RSS Feed de revista