Microstructure morphology and aging characteristics of 9% Cr martensitic heat-resistant steel after service

Zhang Kun

Zhang Kun

China Nuclear Energy Technology Co., Ltd.Beijing, China
Cerca questo autore su
Sciendo|Google Scholar
Kun, Zhang
, 
Cai Wenhe

Cai Wenhe

North China Electric Power Test and Research Institute, China Datang Group General Institute of Science and Technology Co., Ltd.Beijing, China
Cerca questo autore su
Sciendo|Google Scholar
Wenhe, Cai
, 
Wang Zhichun

Wang Zhichun

North China Electric Power Research Institute Co., Ltd.Beijing, China
Cerca questo autore su
Sciendo|Google Scholar
Zhichun, Wang
, 
Xin Chen

Xin Chen

China Nuclear Energy Technology Co., Ltd.Beijing, China
Cerca questo autore su
Sciendo|Google Scholar
Chen, Xin
, 
Fengyuan Shu

Fengyuan Shu

School of Chemical Engineering and Technology, Sun Yat-sen UniversityZhuhai, China
Cerca questo autore su
Sciendo|Google Scholar
Shu, Fengyuan
, 
Shi Yang

Shi Yang

Fire and Rescue InstituteBeijing,
Cerca questo autore su
Sciendo|Google Scholar
Yang, Shi
, 
Jianwei Wang

Jianwei Wang

Fire and Rescue InstituteBeijing,
Cerca questo autore su
Sciendo|Google Scholar
Wang, Jianwei
, 
Li Weili

Li Weili

North China Electric Power Test and Research Institute, China Datang Group General Institute of Science and Technology Co., Ltd.Beijing, China
Cerca questo autore su
Sciendo|Google Scholar
Weili, Li
 e 
Zhang Xin

Zhang Xin

Science and Technology Research Institute, State Power Investment CorporationBeijing, China
Cerca questo autore su
Sciendo|Google Scholar
Xin, Zhang
  
24 dic 2024
Microstructure morphology and aging characteristics of 9% Cr martensitic heat-resistant steel after service's Cover Image
INFORMAZIONI SU QUESTO ARTICOLO
Articolo precedente
Articolo Successivo
Cita
Scarica la copertina
Categoria dell'articolo: Research Article
Pubblicato online: 24 dic 2024
Pagine: 50 - 65
Ricevuto: 02 apr 2024
Accettato: 26 ott 2024
DOI: https://doi.org/10.2478/msp-2024-0044
Parole chiave
© 2024 the Zhang Kun et al., published by Sciendo
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Lingua:
Inglese
Frequenza di pubblicazione:
4 volte all'anno
Argomenti della rivista:
Scienze materiali, Scienze materiali, altro, Nanomateriali, Materiali funzionali ed intelligenti, Caratteristica e proprietà dei materiali
Feed RSS della rivista