Effects of infill density on mechanical properties of additively manufactured chopped carbon fiber reinforced PLA composites

K. Mayandi

K. Mayandi

Department of Mechanical Engineering, Kalasalingam Academy of Research and EducationKrishnankoil, India
Cerca questo autore su
Sciendo|Google Scholar
Mayandi, K.
, 
K. Rigesh

K. Rigesh

Department of Mechanical Engineering, Kalasalingam Academy of Research and EducationKrishnankoil, India
Cerca questo autore su
Sciendo|Google Scholar
Rigesh, K.
, 
Rajini Nagarajan

Rajini Nagarajan

Department of Mechanical Engineering, Kalasalingam Academy of Research and EducationKrishnankoil, India
Cerca questo autore su
Sciendo|Google Scholar
Nagarajan, Rajini
, 
Sikiru O. Ismail

Sikiru O. Ismail

Department of Engineering, Centre for Engineering Research, School of Physics, Engineering and Computer Science, University of HertfordshireHatfield, UK
Cerca questo autore su
Sciendo|Google Scholar
Ismail, Sikiru O.
, 
Kumar Krishnan

Kumar Krishnan

INTI International University, Research Fellow, INTI International UniversityNilai,
Cerca questo autore su
Sciendo|Google Scholar
Krishnan, Kumar
, 
Faruq Mohammad

Faruq Mohammad

Department of Chemistry, College of Science, King Saud UniversityRiyadh, Kingdom of Saudi Arabia
Cerca questo autore su
Sciendo|Google Scholar
Mohammad, Faruq
 e 
Hamad A. Al-Lohedan

Hamad A. Al-Lohedan

Department of Chemistry, College of Science, King Saud UniversityRiyadh, Kingdom of Saudi Arabia
Cerca questo autore su
Sciendo|Google Scholar
Al-Lohedan, Hamad A.
  
08 mag 2024
Effects of infill density on mechanical properties of additively manufactured chopped carbon fiber reinforced PLA composites's Cover Image
INFORMAZIONI SU QUESTO ARTICOLO
Articolo precedente
Articolo Successivo
Cita
Scarica la copertina
Pubblicato online: 08 mag 2024
Pagine: 42 - 51
Ricevuto: 05 gen 2024
Accettato: 17 mar 2024
DOI: https://doi.org/10.2478/msp-2024-0003
Parole chiave
© 2024 K. Mayandi et al., published by Sciendo
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Fig. 1.

(a) Tensile and (b) impact CAD samples
(a) Tensile and (b) impact CAD samples

Fig. 2.

Tensile fractured samples
Tensile fractured samples

Fig. 3.

Tensile strengths of the cCFPC samples
Tensile strengths of the cCFPC samples

Fig. 4.

Stress-strain curves from the tensile test on cCFPC samples
Stress-strain curves from the tensile test on cCFPC samples

Fig. 5.

Tensile moduli of the cCFPC samples
Tensile moduli of the cCFPC samples

Fig. 6.

Flexural fractured samples of the cCFPCs
Flexural fractured samples of the cCFPCs

Fig. 7.

Flexural strengths of the cCFPC samples
Flexural strengths of the cCFPC samples

Fig. 8.

Flexural moduli of the cCFPC samples
Flexural moduli of the cCFPC samples

Fig. 9.

Stress-strain curve from the flexural test on cCFPC samples
Stress-strain curve from the flexural test on cCFPC samples

Fig. 10.

Impact samples of the cCFPC samples
Impact samples of the cCFPC samples

Fig. 11.

Impact strengths of the cCFPC samples
Impact strengths of the cCFPC samples

Fig. 12.

SEM images of the tensile ruptured 3D-printed cCFPC samples with infill densities of 60% at (a) 100x and (b) 500x, as well as 100% at (c) 100x and (d) 500x magnifications
SEM images of the tensile ruptured 3D-printed cCFPC samples with infill densities of 60% at (a) 100x and (b) 500x, as well as 100% at (c) 100x and (d) 500x magnifications
Lingua:
Inglese
Frequenza di pubblicazione:
4 volte all'anno
Argomenti della rivista:
Scienze materiali, Scienze materiali, altro, Nanomateriali, Materiali funzionali ed intelligenti, Caratteristica e proprietà dei materiali
Feed RSS della rivista