CK | 3.1867 | 49.38 | 0.57 | 77.22 |
OK | 0.5512 | 5.61 | 0.29 | 7.44 |
FK | 0.4215 | 1.02 | 0.22 | 1.03 |
PK | 0.9402 | 0.06 | 0.04 | 0.04 |
SK | 0.7728 | 0.53 | 0.12 | 0.23 |
CaK | 1.2703 | 1.03 | 0.07 | 0.52 |
FeK | 0.9234 | 0.98 | 0.11 | 0.31 |
NiK | 0.7966 | 2.74 | 0.14 | 0.91 |
CuK | 0.8837 | 35.27 | 0.52 | 11.68 |
MoL | 0.6979 | 3.38 | 0.29 | 0.62 |
CK | 4.7439 | 67.59 | 0.57 | 89.30 |
OK | 0.4207 | 3.78 | 0.34 | 3.71 |
FK | 0.3612 | 0.63 | 0.27 | 0.53 |
SK | 0.8711 | 0.36 | 0.09 | 0.13 |
CaK | 1.0372 | 1.56 | 0.08 | 0.58 |
CrK | 0.9261 | 0.38 | 0.06 | 0.05 |
FeK | 0.8968 | 0.44 | 0.06 | 0.11 |
NiK | 0.8198 | 1.54 | 0.12 | 0.38 |
CuK | 0.8246 | 21.59 | 0.40 | 4.99 |
MoL | 0.7734 | 2.13 | 0.22 | 0.22 |
Cu + 5Ni + 3Mo + 9CaF2 | 0.21/61 | 0.24/75 | 0.28/153 | 7,500 | Antifriction films have formed on the contact surfaces |
Cast bronze CuSn5ZnPb |
0.37–0.41/388–405 | Plastic deformation | 800–1,000 | Liquid oil smokes and burns |
CK | 2.0816 | 12.57 | 0.71 | 39.81 |
OK | 0.7860 | 4.71 | 0.25 | 9.91 |
FK | 0.5422 | 1.82 | 0.25 | 3.54 |
SK | 0.8207 | 0.23 | 0.22 | 0.31 |
CaK | 1.0503 | 1.47 | 0.09 | 1.35 |
FeK | 1.1168 | 0.47 | 0.11 | 0.30 |
NiK | 0.9799 | 4.58 | 0.22 | 2.80 |
CuK | 0.9441 | 66.84 | 0.80 | 39.23 |
MoL | 0.6776 | 7.31 | 0.64 | 2.75 |