This study investigates the optimal conditions to deposit a thermal barrier coating using micro- and nanopowders in the air plasma spraying (APS) process. The influence of the APS process parameters on the thickness, porosity and hardness of the yttria-stabilized zirconia (YSZ; ZrO2 × 8Y2O3) coatings deposited with a single-electrode plasma gun was determined. The temperature and velocity of melted particles were determined by the DPV diagnostic system to decrease the number of experimental processes. The current and H2 flow rate were changed in this research. Metco-6700 YSZ micropowder has already been used in plasma spray physical vapor deposition. The results of this study suggest the possibility of using it for APS. The particles of this powder are characterized by high temperature (2,700°C–2,900°C) and high speed (>380 m/s). The highest thickness of the coating was obtained with 6 NLPM (normal liter per minute) H2 flow and 800 A current. Difficulties were observed with the feeding of the powder particles at higher H2 flow. The results showed that using APS, deposition of Metco-6609, a nanopowder normally used in suspension plasma spraying, is possible. In this research, this powder was fed using a carrier gas. The coatings were around 40 μm thick and had high porosity. The lowest porosity of the coating was obtained at a current of 600 A and H2 flow rate of 12 NLPM. In the coatings, unmelted spherical particles were also visible.
</abstract>

This study investigates the optimal conditions to deposit a thermal barrier coating using micro- and nanopowders in the air plasma spraying (APS) process. The influence of the APS process parameters on the thickness, porosity and hardness of the yttria-stabilized zirconia (YSZ; ZrO2 × 8Y2O3) coatings deposited with a single-electrode plasma gun was determined. The temperature and velocity of melted particles were determined by the DPV diagnostic system to decrease the number of experimental processes. The current and H2 flow rate were changed in this research. Metco-6700 YSZ micropowder has already been used in plasma spray physical vapor deposition. The results of this study suggest the possibility of using it for APS. The particles of this powder are characterized by high temperature (2,700°C–2,900°C) and high speed (>380 m/s). The highest thickness of the coating was obtained with 6 NLPM (normal liter per minute) H2 flow and 800 A current. Difficulties were observed with the feeding of the powder particles at higher H2 flow. The results showed that using APS, deposition of Metco-6609, a nanopowder normally used in suspension plasma spraying, is possible. In this research, this powder was fed using a carrier gas. The coatings were around 40 μm thick and had high porosity. The lowest porosity of the coating was obtained at a current of 600 A and H2 flow rate of 12 NLPM. In the coatings, unmelted spherical particles were also visible.

Influence of air plasma spraying process parameters on the thermal barrier coating deposited with micro- and nanopowders

Research and Development Laboratory for Aerospace Materials

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

This study investigates the optimal conditions to deposit a thermal barrier coating using micro- and nanopowders in the air plasma spraying (APS) process. The...

Influence of air plasma spraying process parameters on the thermal barrier coating deposited with micro- and nanopowders

Publié en ligne: 31 déc. 2022

Pages: 80 - 92

Reçu: 03 oct. 2022

Accepté: 13 déc. 2022

DOI: https://doi.org/10.2478/msp-2022-0034

Mots clés
thermal barrier coatings, air plasma spraying, yttria-stabilized zirconia, nanopowders

© 2022 Tadeusz Kubaszek et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Influence of air plasma spraying process parameters on the thermal barrier coating deposited with micro- and nanopowders

Publié en ligne: 31 déc. 2022

Pages: 80 - 92

Reçu: 03 oct. 2022

Accepté: 13 déc. 2022

DOI: https://doi.org/10.2478/msp-2022-0034

Mots clésthermal barrier coatings, air plasma spraying, yttria-stabilized zirconia, nanopowders

© 2022 Tadeusz Kubaszek et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Mots clés
thermal barrier coatings, air plasma spraying, yttria-stabilized zirconia, nanopowders