<p>The hereby work presents the iron-nickel alloys electroplated on the different metallic substrates (aluminium, silver, brass) using galvanostatic deposition, with and without presence of the external magnetic field (EMF). The films were obtained in the same electrochemical bath composition - mixture of iron and nickel sulphates (without presence of additives) in the molar ratio of 2 : 1 (Ni : Fe), the electric current density (50.0 mA/cm<sup>2</sup>), and the time (3600 s). The mutual alignment of the electric (E) and magnetic field (B) was changeable - parallel and perpendicular. The source of EMF was a set of two permanent magnets (magnetic field strength ranged from 80 mT to 400 mT). It was analysed the surface microstructure, composition, morphology, thickness and the mechanical properties (roughness, work of adhesion). The surface morphology and the thickness of films were observed by Scanning Electron Microscopy (SEM) and Confocal Laser Scanning Microscopy (CLSM). The elemental composition of all FeNi films was measured using Wavelength Dispersive X-Ray Fluorescence (WDXRF). The crystalographic analysis of the deposits was carried out by X-Ray Diffraction. Depending on the used substrate, modified external magnetic field orientation influenced the tribological and physio-chemical properties of the deposited layers. The diamagnetic substrates and EMF application reduced the FeNi thickness and the average crystallites size, in contrast to the paramagnetic substrate. Parallel EMF increased the value of the tribological parameters for CuZn and Ag but decreased for Al. The content of FeNi structure was rising in the case of diamagnetic substrate and the dependence was opposite on the paramagnetic substrate.</p>
</abstract>

The hereby work presents the iron-nickel alloys electroplated on the different metallic substrates (aluminium, silver, brass) using galvanostatic deposition, with and without presence of the external magnetic field (EMF). The films were obtained in the same electrochemical bath composition - mixture of iron and nickel sulphates (without presence of additives) in the molar ratio of 2 : 1 (Ni : Fe), the electric current density (50.0 mA/cm2), and the time (3600 s). The mutual alignment of the electric (E) and magnetic field (B) was changeable - parallel and perpendicular. The source of EMF was a set of two permanent magnets (magnetic field strength ranged from 80 mT to 400 mT). It was analysed the surface microstructure, composition, morphology, thickness and the mechanical properties (roughness, work of adhesion). The surface morphology and the thickness of films were observed by Scanning Electron Microscopy (SEM) and Confocal Laser Scanning Microscopy (CLSM). The elemental composition of all FeNi films was measured using Wavelength Dispersive X-Ray Fluorescence (WDXRF). The crystalographic analysis of the deposits was carried out by X-Ray Diffraction. Depending on the used substrate, modified external magnetic field orientation influenced the tribological and physio-chemical properties of the deposited layers. The diamagnetic substrates and EMF application reduced the FeNi thickness and the average crystallites size, in contrast to the paramagnetic substrate. Parallel EMF increased the value of the tribological parameters for CuZn and Ag but decreased for Al. The content of FeNi structure was rising in the case of diamagnetic substrate and the dependence was opposite on the paramagnetic substrate.

Substrates with Different Magnetic Properties Versus Iron-Nickel Film Electrodeposition

AGH University of Science and Technology in Kraków

Chemistry-Didactics-Ecology-Metrology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

The hereby work presents the iron-nickel alloys electroplated on the different metallic substrates (aluminium, silver, brass) using galvanostatic deposition,...

Substrates with Different Magnetic Properties Versus Iron-Nickel Film Electrodeposition

Publié en ligne: 25 janv. 2024

Pages: 157 - 170

DOI: https://doi.org/10.2478/cdem-2023-0009

Mots clés
electrodeposition, magnetic field, magnetohydrodynamics, substrate, thin films, iron-nickel alloys

© 2023 Anna M. Białostocka et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Substrates with Different Magnetic Properties Versus Iron-Nickel Film Electrodeposition

Publié en ligne: 25 janv. 2024

Pages: 157 - 170

DOI: https://doi.org/10.2478/cdem-2023-0009

Mots cléselectrodeposition, magnetic field, magnetohydrodynamics, substrate, thin films, iron-nickel alloys

© 2023 Anna M. Białostocka et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Mots clés
electrodeposition, magnetic field, magnetohydrodynamics, substrate, thin films, iron-nickel alloys