<p>Eddy current (EC) method is considered as most applicable for in-service detection of fatigue subsurface cracks initiated in aircraft multilayer structures near the rivet holes. At the same time, the successful solution of this problem is obstructed by additional noise created by defect-free rivets. All EC inspection techniques for the detection of subsurface cracks around the rivets can be classified into three main groups: 1) static mode – carried out by placing the EC probe concentrically on the rivet head; 2) rotational mode – when the EC probe is rotated around the rivet axle and 2) sliding mode – performed by the movement of EC probe along the rivet line or near it. All these approaches have some advantages and limitations. In this study, known EC techniques for the detection of cracks in multilayer aircraft structures are analyzed. New advanced EC techniques for the detection of fatigue cracks in internal layers of the riveted structures based on different types (ring, sliding, and rotational) probes are presented. The static EC method with developed low-height ring-type probe creates the possibility to detect cracks in the difficult of access areas. The possibility to estimate the length of detected cracks by a ring-type probe is shown. The proposed rotational remote field EC probe can detect as small as 1.0 mm long cracks under the button-head rivet and 2 mm thick upper skin with a high signal-to-noise ratio. Therefore, in many aircraft structures, fatigue cracks will be detected before a critical threshold achieved. New EC sliding techniques based on remote field and double differential probes were proposed for the rapid detection of cracks in internal layers of riveted aircraft structures. Remote-field EC probe for reliable detection of fatigue cracks in third and fourth layers of five-layer units was proposed. Another sliding technique based on a double differential EC probe gives the possibility to detect transverse cracks in the second layer without the rivet row area access. The main advantage of developed techniques is high inspection reliability due to the possibility to discriminate the signals created by cracks and defect-free rivets. Presented inspection procedures include the selective signal analysis in the complex plane diagram. Proposed EC inspection techniques were successfully implemented into the aircraft maintenance practice.</p>
</abstract>

Eddy current (EC) method is considered as most applicable for in-service detection of fatigue subsurface cracks initiated in aircraft multilayer structures near the rivet holes. At the same time, the successful solution of this problem is obstructed by additional noise created by defect-free rivets. All EC inspection techniques for the detection of subsurface cracks around the rivets can be classified into three main groups: 1) static mode – carried out by placing the EC probe concentrically on the rivet head; 2) rotational mode – when the EC probe is rotated around the rivet axle and 2) sliding mode – performed by the movement of EC probe along the rivet line or near it. All these approaches have some advantages and limitations. In this study, known EC techniques for the detection of cracks in multilayer aircraft structures are analyzed. New advanced EC techniques for the detection of fatigue cracks in internal layers of the riveted structures based on different types (ring, sliding, and rotational) probes are presented. The static EC method with developed low-height ring-type probe creates the possibility to detect cracks in the difficult of access areas. The possibility to estimate the length of detected cracks by a ring-type probe is shown. The proposed rotational remote field EC probe can detect as small as 1.0 mm long cracks under the button-head rivet and 2 mm thick upper skin with a high signal-to-noise ratio. Therefore, in many aircraft structures, fatigue cracks will be detected before a critical threshold achieved. New EC sliding techniques based on remote field and double differential probes were proposed for the rapid detection of cracks in internal layers of riveted aircraft structures. Remote-field EC probe for reliable detection of fatigue cracks in third and fourth layers of five-layer units was proposed. Another sliding technique based on a double differential EC probe gives the possibility to detect transverse cracks in the second layer without the rivet row area access. The main advantage of developed techniques is high inspection reliability due to the possibility to discriminate the signals created by cracks and defect-free rivets. Presented inspection procedures include the selective signal analysis in the complex plane diagram. Proposed EC inspection techniques were successfully implemented into the aircraft maintenance practice.

Detection of the Fatigue Cracks Initiated near the Rivet Holes by Eddy Current Inspection Techniques

Karpenko Physico-Mechanical Institute of National Academy of Sciences of Ukraine

Transactions on Aerospace Research

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Eddy current (EC) method is considered as most applicable for in-service detection of fatigue subsurface cracks initiated in aircraft multilayer structures...

Detection of the Fatigue Cracks Initiated near the Rivet Holes by Eddy Current Inspection Techniques

Publicado en línea: 24 jul 2020

Páginas: 47 - 58

DOI: https://doi.org/10.2478/tar-2020-0010

Palabras clave
eddy current (EC), EC probe, rivet, multilayer aircraft structure, fatigue crack, operational frequency

© 2017 Copyright by Lukasiewicz Research Network – Institute of Aviation

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Detection of the Fatigue Cracks Initiated near the Rivet Holes by Eddy Current Inspection Techniques

Publicado en línea: 24 jul 2020

Páginas: 47 - 58

DOI: https://doi.org/10.2478/tar-2020-0010

Palabras claveeddy current (EC), EC probe, rivet, multilayer aircraft structure, fatigue crack, operational frequency

© 2017 Copyright by Lukasiewicz Research Network – Institute of Aviation

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Palabras clave
eddy current (EC), EC probe, rivet, multilayer aircraft structure, fatigue crack, operational frequency