<abstract xmlns="http://www.w3.org/1999/xhtml">Amorphous precursors of A: (Fe64Co21B15)95P4Cu1 and B: (Fe64Co21B15)96P4 alloys were used. Nanocrystalline structure was created by heat treatment. Samples were studied by Mössbauer spectroscopy, XRD and AFM. Cu ions of dose 1016 at/cm2 were implanted into the amorphous B. According to simulated program we estimated that Cu ions created surface layer with a thickness of a few micrometres. Changes in bulk structure were not observed at parameters of Mössbauer spectra after implantation. After heat treatment the implanted sample was nearly identical with the nanocrystalline sample of A. Implantation had an influence on the volumetric fraction of the constituent phases and on their magnetic microstructure. Implantation of Cu ions in amorphous precursor containing Cu as A caused after heat treatment in nanocrystalline state increasing of nanocrystalline component. This technology of preparation of nanocrystalline alloys indicate that implantation of ions into an amorphous precursor has an influence on the final structure and properties of nanocrystalline alloy.</abstract>

Amorphous precursors of A: (Fe64Co21B15)95P4Cu1 and B: (Fe64Co21B15)96P4 alloys were used. Nanocrystalline structure was created by heat treatment. Samples were studied by Mössbauer spectroscopy, XRD and AFM. Cu ions of dose 1016 at/cm2 were implanted into the amorphous B. According to simulated program we estimated that Cu ions created surface layer with a thickness of a few micrometres. Changes in bulk structure were not observed at parameters of Mössbauer spectra after implantation. After heat treatment the implanted sample was nearly identical with the nanocrystalline sample of A. Implantation had an influence on the volumetric fraction of the constituent phases and on their magnetic microstructure. Implantation of Cu ions in amorphous precursor containing Cu as A caused after heat treatment in nanocrystalline state increasing of nanocrystalline component. This technology of preparation of nanocrystalline alloys indicate that implantation of ions into an amorphous precursor has an influence on the final structure and properties of nanocrystalline alloy.

Formation of nanocrystalline alloys after Cu ions implantation into amorphous precursor

Institute of Nuclear and Physical Engineering

Journal of Electrical Engineering

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Amorphous precursors of A: (Fe64Co21B15)95P4Cu1 and B: (Fe64Co21B15)96P4 alloys were used. Nanocrystalline structure was created by heat treatment. Samples...

Formation of nanocrystalline alloys after Cu ions implantation into amorphous precursor

Publicado en línea: 13 may 2019

Páginas: 171 - 175

Recibido: 17 dic 2018

DOI: https://doi.org/10.2478/jee-2019-0025

Palabras clave
amorphous alloys, nanocrystalline alloys, radiation damage, Mössbauer spectroscopy

© 2019 Jozef Sitek et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Formation of nanocrystalline alloys after Cu ions implantation into amorphous precursor

Publicado en línea: 13 may 2019

Páginas: 171 - 175

Recibido: 17 dic 2018

DOI: https://doi.org/10.2478/jee-2019-0025

Palabras claveamorphous alloys, nanocrystalline alloys, radiation damage, Mössbauer spectroscopy

© 2019 Jozef Sitek et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Palabras clave
amorphous alloys, nanocrystalline alloys, radiation damage, Mössbauer spectroscopy