<p>Alloys of FeNiSiB soft magnetic materials containing variable Fe and Ni contents (wt.%) have been produced by melt spinning method, a kind of rapid solidification technique. The magnetic and structural properties of FeNiSiB alloys with soft magnetic properties were investigated by increasing the Fe ratio. X-ray diffraction analysis and SEM images shows that the produced alloy ribbons generally have an amorphous structure, together with also partially nanocrystalline regions. It was observed that the structure became much more amorphous together with increasing Fe content in the composition. Among the alloy ribbons, the highest saturation magnetization was obtained as 0.6 emu/g in the specimen with 50 wt.% Fe. In addition, the highest Curie temperature was observed in the sample containing 46 wt.% Fe.</p>
</abstract>

Alloys of FeNiSiB soft magnetic materials containing variable Fe and Ni contents (wt.%) have been produced by melt spinning method, a kind of rapid solidification technique. The magnetic and structural properties of FeNiSiB alloys with soft magnetic properties were investigated by increasing the Fe ratio. X-ray diffraction analysis and SEM images shows that the produced alloy ribbons generally have an amorphous structure, together with also partially nanocrystalline regions. It was observed that the structure became much more amorphous together with increasing Fe content in the composition. Among the alloy ribbons, the highest saturation magnetization was obtained as 0.6 emu/g in the specimen with 50 wt.% Fe. In addition, the highest Curie temperature was observed in the sample containing 46 wt.% Fe.

Effect of Fe-Ni Substitution in FeNiSiB Soft Magnetic Alloys Produced by Melt Spinning

Department of Fundamental Sciences and Engineering

Sivas University of Science and Technology

Department of Materials Sciences and Engineering

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Alloys of FeNiSiB soft magnetic materials containing variable Fe and Ni contents (wt.%) have been produced by melt spinning method, a kind of rapid...

Effect of Fe-Ni Substitution in FeNiSiB Soft Magnetic Alloys Produced by Melt Spinning

Publicado en línea: 30 dic 2021

Páginas: 79 - 89

DOI: https://doi.org/10.2478/adms-2021-0026

Palabras clave
Alloy design, Curie temperature, FeNiSiB alloys, melt spinning, saturation magnetization

© 2021 Muhammed Fatih Kılıçaslan et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Effect of Fe-Ni Substitution in FeNiSiB Soft Magnetic Alloys Produced by Melt Spinning

Publicado en línea: 30 dic 2021

Páginas: 79 - 89

DOI: https://doi.org/10.2478/adms-2021-0026

Palabras claveAlloy design, Curie temperature, FeNiSiB alloys, melt spinning, saturation magnetization

© 2021 Muhammed Fatih Kılıçaslan et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Palabras clave
Alloy design, Curie temperature, FeNiSiB alloys, melt spinning, saturation magnetization