Transparent europium niobate EuNbO4 (ENOF) thin film (~100 nm) was prepared by sol-gel/spin-coating process on alumina substrates with PbZrO3 (PZ) interlayer and annealing at 1000°C. The X-ray diffraction (XRD) analyses verified the formation of the monoclinic M-EuNbO4 and tetragonal T-EuNb5O14 phases in ENO precursor and ENOF film. The surface morphology of powder precursor and microstructure of film were investigated by SEM analyses. Surface chemistry was investigated by X-ray photoelectron spectroscopy (XPS). The XPS demonstrated two valence states of Eu (Eu3+/Eu2+) in powder precursor as nanophosphor for lighting and display technologies. Eu concentration (at. %) decreases from 10 % in the precursor to 2 % in the film considering the substrate contains C, Al, Si, Pb, and Zr elements (40 %) at Nb (6 %) and O (52 %). The single valence state of Eu3+ was confirmed in ENO film designed for the application in environmental electrolytic thin-film devices.
</abstract>

Transparent europium niobate EuNbO4 (ENOF) thin film (~100 nm) was prepared by sol-gel/spin-coating process on alumina substrates with PbZrO3 (PZ) interlayer and annealing at 1000°C. The X-ray diffraction (XRD) analyses verified the formation of the monoclinic M-EuNbO4 and tetragonal T-EuNb5O14 phases in ENO precursor and ENOF film. The surface morphology of powder precursor and microstructure of film were investigated by SEM analyses. Surface chemistry was investigated by X-ray photoelectron spectroscopy (XPS). The XPS demonstrated two valence states of Eu (Eu3+/Eu2+) in powder precursor as nanophosphor for lighting and display technologies. Eu concentration (at. %) decreases from 10 % in the precursor to 2 % in the film considering the substrate contains C, Al, Si, Pb, and Zr elements (40 %) at Nb (6 %) and O (52 %). The single valence state of Eu3+ was confirmed in ENO film designed for the application in environmental electrolytic thin-film devices.

X-ray Photoelectron Spectroscopy Study of Europium Niobate Thin Film Prepared by Chemical Solution Deposition

Powder Metallurgy Progress

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Transparent europium niobate EuNbO4 (ENOF) thin film (~100 nm) was prepared by sol-gel/spin-coating process on alumina substrates with PbZrO3 (PZ) interlayer...

X-ray Photoelectron Spectroscopy Study of Europium Niobate Thin Film Prepared by Chemical Solution Deposition

Online veröffentlicht: 17. März 2022

Seitenbereich: 94 - 103

DOI: https://doi.org/10.2478/pmp-2020-0009

Schlüsselwörter
sol-gel, thin films, EuNbO, microstructure, Spectroscopy, XPS

© 2020 Helena Bruncková et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

X-ray Photoelectron Spectroscopy Study of Europium Niobate Thin Film Prepared by Chemical Solution Deposition

Online veröffentlicht: 17. März 2022

Seitenbereich: 94 - 103

DOI: https://doi.org/10.2478/pmp-2020-0009

Schlüsselwörtersol-gel, thin films, EuNbO, microstructure, Spectroscopy, XPS

© 2020 Helena Bruncková et al., published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Schlüsselwörter
sol-gel, thin films, EuNbO, microstructure, Spectroscopy, XPS