Sample Name | Wear rate (mm3/Nm) (10−6) | Volume loss (mm3) (103) | Coefficient of Friction (COF) |
---|---|---|---|
0 g/l saccharin | 11.24 | 5.620 | 0.483 |
0.5 g/l saccharin | 5.91 | 2.953 | 0.528 |
1 g/l saccharin | 4.93 | 3.002 | 0.535 |
2 g/l saccharin | 3.75 | 1.875 | 0.563 |
ECorr (mV) | Icorr ( |
Corrosion rate (mm/year) | |
---|---|---|---|
AISI 1040 | −770 | 91.73 | 1.08 |
0 g/l Saccharin | −719 | 65.18 | 0.77 |
0.5 g/l Saccharin | −678 | 58.26 | 0.68 |
1 g/l Saccharin | −662 | 38.18 | 0.44 |
2 g/l Saccharin | −658 | 56.53 | 0.66 |
Sample | 2 (Degree) | Full width at half maximum (FWHM) | Grain size (D) (nm) |
---|---|---|---|
0 g/l Saccharin | 44.28 | 0.650 | 32.42 |
0.5 g/l Saccharin | 44.44 | 0.960 | 21.87 |
1 g/l Saccharin | 44.46 | 0.875 | 23.99 |
2 g/l Saccharin | 44.47 | 0.644 | 32.58 |
Parameter | Amount |
---|---|
Current density | 200 mA/cm2 |
Ultrasonic mixing | 5 min |
Temperature | 40°C |
Mixing speed | 100 rpm |
pH | 2.5 |
hc (nm) | Pmax ( |
S ( |
A (nm2) | Hmax (nm) | Er (GPa) | H (GPa) | Residual Stress (Gpa) | |
---|---|---|---|---|---|---|---|---|
0 g/l Sacc. | 317 | 5006 | 326 | 2842233 | 329 | 171.58 | 1.76 | 0.51 |
0.5 g/l Sacc. | 304 | 5005 | 257 | 2632610 | 319 | 140.58 | 1.90 | 0.24 |
1 g/l Sacc. | 250 | 5007 | 99 | 1819289 | 281 | 65.17 | 2.75 | −0.95 |
2 g/l Sacc. | 242 | 5008 | 136 | 1706650 | 269 | 92.11 | 2.93 | −0.71 |
C | Si | Mn | Fe | Pmax | Smax |
---|---|---|---|---|---|
0.419 | 0.254 | 0.751 | 98 | 0.040 | 0.050 |
Rs (Ω.cm2) | Rp (Ω.cm2) | n | Yo(10−4) (Ω−1.cm−2.sn) | CP ( |
|
---|---|---|---|---|---|
AISI 1040 | 214 | 2328 | 0.42 | 5.85 | 89.6 |
0 g/l Saccharin | 161 | 2615 | 0.53 | 6.08 | 91.8 |
0.5 g/l Saccharin | 195 | 4371 | 0.67 | 2.95 | 33.4 |
1 g/l Saccharin | 145 | 5520 | 0.67 | 2.70 | 32.9 |
2 g/l Saccharin | 166 | 5472 | 0.59 | 2.67 | 34.7 |
Bath solution | Amount | Function |
---|---|---|
NiSO4.7H2O (nickel sulphate) | 50 g/l | Ni2+ source |
NiCl2.6H2O (nickel chloride) | 45 g/l | Ni2+ source |
CrCl3. 6H2O (chromium chloride) | 75 g/l | Cr3+ source |
H3BO3 (boric acid) | 50 g/l | Blocking agent |
C6H8O7 (citric acid) | 70 g/l | Blocking agent |
Na3C6H5O7.2H2O (sodium citrate dihydrate) | 105 g/l | Complexing agent |
C7H4NNaO3S • 2H2O (sodium saccharin) | 0, 0.5, 1, 2 g/l | Additive material |
C | N | O | Na | S | Cr | Ni | |
---|---|---|---|---|---|---|---|
0 g/l Saccharin | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 1.18 | 98.82 |
0.5 g/l Saccharin | 7.83 | 2.27 | 1.77 | 0.17 | 0.17 | 2.53 | 85.27 |
1 g/l Saccharin | 8.64 | 2.37 | 0.00 | 0.13 | 0.19 | 2.84 | 85.83 |
2 g/l Saccharin | 7.87 | 1.85 | 0.29 | 0.19 | 0.22 | 3.38 | 86.21 |
Chemical formula | 2-theta (deg) | Phase name | DB card number | Chemical formula | 2-theta (deg) | Phase name | DB card number | ||
---|---|---|---|---|---|---|---|---|---|
18.7 | 100 | 44.4 | 111 | ||||||
26.3 | 110 | 01-089-2392 | ■ | Ni | 51.8 | 200 | 00-004-0850 | ||
▲ | Cr | 44.4 | 210 | 01-077-7591 | 76.3 | 220 | |||
51.7 | 200 | 44.4 | 111 | ||||||
76.3 | 220 | • | (Cr2Ni23)0.16 | 51.8 | 200 | 01-077-7616 | |||
♦ | Cr7Ni3 | 42.6 | 410 | 00-051-0637 | 76.3 | 220 |