<abstract xmlns="http://www.w3.org/1999/xhtml">

<p>In the study, the morphological properties of polyacrylonitrile (PAN) fibers produced by electrospinning at different needle diameters and solution flow rates were investigated. For this purpose, 20G and 22G diameter needles were used. The fibres were produced at flow rates of 0.5 ml/hr, 1 ml/hr and 1.5 ml/hr. Scanning electron microscopy (SEM) was used to measure nanofiber diameters. Statistical analyzes were made with the help of the SPSS program. It was observed that finer fibers were obtained as the needle diameter decreased. As the solution flow rate increased, thicker fibers were obtained. In addition, it was observed that the needle diameter and flow rate affect the fiber arrangement and interfiber spacing.</p>
</abstract>

In the study, the morphological properties of polyacrylonitrile (PAN) fibers produced by electrospinning at different needle diameters and solution flow rates were investigated. For this purpose, 20G and 22G diameter needles were used. The fibres were produced at flow rates of 0.5 ml/hr, 1 ml/hr and 1.5 ml/hr. Scanning electron microscopy (SEM) was used to measure nanofiber diameters. Statistical analyzes were made with the help of the SPSS program. It was observed that finer fibers were obtained as the needle diameter decreased. As the solution flow rate increased, thicker fibers were obtained. In addition, it was observed that the needle diameter and flow rate affect the fiber arrangement and interfiber spacing.

Investigation of the Effect of Needle Diameter and the Solution Flow Rate on Fiber Morphology in the Electrospinning Method

Fibres & Textiles in Eastern Europe

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

In the study, the morphological properties of polyacrylonitrile (PAN) fibers produced by electrospinning at different needle diameters and solution flow rates...

Investigation of the Effect of Needle Diameter and the Solution Flow Rate on Fiber Morphology in the Electrospinning Method

Article Category: Research Article

Online veröffentlicht: 18. Okt. 2023

Seitenbereich: 22 - 29

DOI: https://doi.org/10.2478/ftee-2023-0032

Schlüsselwörter
electrospinning, needle diameter, solution flow rate, nanofiber diameter, PAN

© 2023 Łukasiewicz Research Network-Łódź Institute of Technology, published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Investigation of the Effect of Needle Diameter and the Solution Flow Rate on Fiber Morphology in the Electrospinning Method

Article Category: Research Article

Online veröffentlicht: 18. Okt. 2023

Seitenbereich: 22 - 29

DOI: https://doi.org/10.2478/ftee-2023-0032

Schlüsselwörterelectrospinning, needle diameter, solution flow rate, nanofiber diameter, PAN

© 2023 Łukasiewicz Research Network-Łódź Institute of Technology, published by Sciendo

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
electrospinning, needle diameter, solution flow rate, nanofiber diameter, PAN