<abstract xmlns="http://www.w3.org/1999/xhtml"><p> New materials obtained by pyrolysis of gelatine (G) and poly(1,2-dimethylsilazane) (PSN) (weight ratio: G/PSN 70/30) at temperatures 700 and 900 °C were characterized by SEM and Raman spectroscopy. The presence of ceramics influences on the cluster size of the materials. Electrochemical tests were performed by cyclic voltammetry and galvanostatic cyclic polarization. The capacity of G/PSN was 464 and 527 mAh/g for materials pyrolysed at 700 and 900 °C. The capacity fading was 1 % after 17<sup>th</sup> cycle for G/PSN at 900 °C. This value is higher of 185 mAh/g in comparison to capacity of gelatine pyrolysed at the same conditions.</p></abstract>

New materials obtained by pyrolysis of gelatine (G) and poly(1,2-dimethylsilazane) (PSN) (weight ratio: G/PSN 70/30) at temperatures 700 and 900 °C were characterized by SEM and Raman spectroscopy. The presence of ceramics influences on the cluster size of the materials. Electrochemical tests were performed by cyclic voltammetry and galvanostatic cyclic polarization. The capacity of G/PSN was 464 and 527 mAh/g for materials pyrolysed at 700 and 900 °C. The capacity fading was 1 % after 17th cycle for G/PSN at 900 °C. This value is higher of 185 mAh/g in comparison to capacity of gelatine pyrolysed at the same conditions.

Electrochemical Characterization of Gelatine Derived Ceramics

Gdansk University of Technology, Chemical Faculty, Department of Chemistry and Technology of Functional Materials, Narutowicza 11/12, 80-233 Gdańsk, Poland

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Electrochemical Characterization of Gelatine Derived Ceramics"}

New materials obtained by pyrolysis of gelatine (G) and poly(1,2-dimethylsilazane) (PSN) (weight ratio: G/PSN 70/30) at temperatures 700 and 900 °C were...

Electrochemical Characterization of Gelatine Derived Ceramics

Online veröffentlicht: 20. Dez. 2014

Seitenbereich: 75 - 81

DOI: https://doi.org/10.2478/adms-2014-0023