s | Pcryst [MPa] | ||
---|---|---|---|
273.15 K | 283.15 K | 293.15 K | |
1 | 0 | 0 | 0 |
1.1 | 12.76 | 13.23 | 13.69 |
1.5 | 54.28 | 56.27 | 58.26 |
2 | 92.80 | 96.19 | 99.59 |
5 | 215.46 | 223.35 | 231.24 |
10 | 308.26 | 319.54 | 330.83 |
Pa [MPa] | 1.0 | 2.0 | 3.0 | 4.0 | 5.0 | 6.0 | 7.0 | 15.0 | 20.0 |
σt [MPa] | 1.07 | 2.15 | 3.22 | 4.3 | 5.37 | 6.44 | 7.52 | 16.11 | 21.4 |
Share in pore radii range [%] | Total open porosity [%] | Corresponding radius “ai” [cm] | Modeled porosity [%] |
---|---|---|---|
3.15 | a0 = 0.206 | P0 = 0.8719 | |
23.96 | 27.68 | a1= 0.405 | P1 = 6.6321 |
62.08 | a2 = 0.556 | P2 =17.1837 | |
10.81 | a3 = 0.310 | P3 = 2.9922 |
s | Pcryst [MPa] | ||
---|---|---|---|
273.15 K | 283.15 K | 293.15 K | |
1 | 0 | 0 | 0 |
1.1 | 16.88 | 17.50 | 18.12 |
1.5 | 71.83 | 74.46 | 77.09 |
2 | 122.79 | 127.28 | 131.79 |
5 | 285.10 | 295.54 | 305.98 |
10 | 407.89 | 422.83 | 437.76 |
a | P for b=1 | σt | a | P for b=1.25 | σt | a | P for b=1.5 | σt |
---|---|---|---|---|---|---|---|---|
0.1 | 0.001 | 0.502 | 0.1 | 0.000512 | 0.501 | 0.1 | 0.000296 | 0.5 |
0.15 | 0.003375 | 0.505 | 0.15 | 0.001728 | 0.503 | 0.15 | 0.001 | 0.502 |
0.2 | 0.008 | 0.512 | 0.2 | 0.004096 | 0.506 | 0.2 | 0.002370 | 0.504 |
0.25 | 0.015625 | 0.524 | 0.25 | 0.008 | 0.512 | 0.25 | 0.004629 | 0.507 |
0.3 | 0.027 | 0.542 | 0.3 | 0.013824 | 0.521 | 0.3 | 0.008 | 0.512 |
0.35 | 0.042875 | 0.567 | 0.35 | 0.021952 | 0.534 | 0.35 | 0.012704 | 0.519 |
0.4 | 0.064 | 0.603 | 0.4 | 0.032768 | 0.551 | 0.4 | 0.018963 | 0.529 |
0.5 | 0.125 | 0.714 | 0.5 | 0.064 | 0.603 | 0.5 | 0.037037 | 0.558 |
0.6 | 0.216 | 0.913 | 0.6 | 0.110592 | 0.687 | 0.6 | 0.064 | 0.603 |
0.7 | 0.343 | 1.283 | 0.7 | 0.175616 | 0.82 | 0.7 | 0.10163 | 0.67 |
0.8 | 0.512 | 2.074 | 0.8 | 0.262144 | 1.033 | 0.8 | 0.151704 | 0.768 |
0.9 | 0.729 | 4.535 | 0.9 | 0.373248 | 1.393 | 0.9 | 0.216 | 0.913 |
a | P for b=1.75 | σt | a | P for b=2 | σt | a | P for b=3 | σt |
---|---|---|---|---|---|---|---|---|
0.1 | 0.000187 | 0.5 | 0.1 | 0.000125 | 0.5 | 0.1 | 0.000037 | 0.5 |
0.15 | 0.000630 | 0.501 | 0.15 | 0.000422 | 0.501 | 0.15 | 0.000125 | 0.5 |
0.2 | 0.001 | 0.502 | 0.2 | 0.001 | 0.502 | 0.2 | 0.000296 | 0.5 |
0.25 | 0.002915 | 0.504 | 0.25 | 0.001953 | 0.503 | 0.25 | 0.000578 | 0.501 |
0.3 | 0.005038 | 0.508 | 0.3 | 0.003375 | 0.505 | 0.3 | 0.001 | 0.502 |
0.35 | 0.008 | 0.512 | 0.35 | 0.005359 | 0.508 | 0.35 | 0.00158 | 0.5023 |
0.4 | 0.011942 | 0.518 | 0.4 | 0.008 | 0.512 | 0.4 | 0.00237 | 0.504 |
0.5 | 0.023324 | 0.536 | 0.5 | 0.015625 | 0.524 | 0.5 | 0.00462 | 0.507 |
0.6 | 0.040303 | 0.563 | 0.6 | 0.027 | 0.542 | 0.6 | 0.008 | 0.512 |
0.7 | 0.064 | 0.603 | 0.7 | 0.042875 | 0.567 | 0.7 | 0.0127 | 0.519 |
0.8 | 0.095534 | 0.658 | 0.8 | 0.064 | 0.603 | 0.8 | 0.019 | 0.529 |
0.9 | 0.136023 | 0.736 | 0.9 | 0.091125 | 0.65 | 0.9 | 0.027 | 0.542 |
s | Pcryst [MPa] | ||
---|---|---|---|
273.15 K | 283.15 K | 293.15 K | |
1 | 0 | 0 | 0 |
1.1 | 4.35 | 4.51 | 4.67 |
1.5 | 18.52 | 19.20 | 19.88 |
2 | 31.66 | 32.82 | 33.98 |
5 | 73.52 | 76.21 | 78.90 |
10 | 105.18 | 109.03 | 112.88 |
s | Pcryst [MPa] | ||
---|---|---|---|
273.15 K | 283.15 K | 293.15 K | |
1.000 | 0 | 0 | 0 |
1.001 | 0.12 | 0.13 | 0.13 |
1.002 | 0.25 | 0.25 | 0.26 |
1.003 | 0.37 | 0.38 | 0.39 |
1.004 | 0.49 | 0.51 | 0.53 |
1.005 | 0.61 | 0.63 | 0.66 |
1.006 | 0.73 | 0.76 | 0.79 |
1.007 | 0.86 | 0.89 | 0.92 |
1.008 | 0.98 | 1.01 | 1.05 |
1.009 | 1.1 | 1.14 | 1.18 |
1.01 | 1.22 | 1.26 | 1.31 |
1.02 | 2.43 | 2.52 | 2.61 |
1.03 | 3.63 | 3.76 | 3.89 |
1.04 | 4.81 | 4.99 | 5.16 |
1.05 | 5.98 | 6.2 | 6.42 |
1.06 | 7.15 | 7.41 | 7.67 |
1.07 | 8.3 | 8.6 | 8.91 |
1.08 | 9.44 | 9.78 | 10.1 |
1.09 | 10.6 | 11 | 11.3 |
1.1 | 11.7 | 12.1 | 12.5 |
1.5 | 49.7 | 51.5 | 53.4 |
2 | 85 | 88.1 | 91.2 |
5 | 197 | 205 | 212 |
10 | 282 | 293 | 303 |
σt [MPa] | Pa [MPa] | ||||||||
---|---|---|---|---|---|---|---|---|---|
a [cm] | 1.0 | 2.0 | 3.0 | 4.0 | 5.0 | 6.0 | 7.0 | 15.0 | 20.0 |
0.206 | 0.51 | 1.03 | 1.54 | 2.05 | 2.57 | 3.08 | 3.59 | 7.70 | 10.30 |
0.310 | 0.55 | 1.09 | 1.64 | 2.18 | 2.73 | 3.28 | 3.82 | 8.19 | 10.90 |
0.398 | 0.60 | 1.20 | 1.80 | 2.40 | 3.00 | 3.61 | 4.21 | 9.01 | 12.02 |
0.398 | 0.81 | 1.62 | 2.43 | 3.25 | 4.06 | 4.87 | 5.68 | 12.2 | 16.23 |
Tested parameter | Unit | Sample 2 | Sample 3 | |
---|---|---|---|---|
Total surface area | m2/g | 1.837 | 1.440 | |
Volume median pore diameter | μm | 1.28 | 1.84 | |
Apparent density | g/ml | 1.89 | 1.79 | |
Specific gravity | g/ml | 2.55 | 2.48 | |
Open porosity | % | 26.01 | 27.68 | |
Permeability | mdarcy | 57.0 | 68.3 | |
Tortuosity | - | 9.7 | 9.1 | |
Pore size distribution | ||||
P3 | > 90 μm | % | 6.21 | 5.42 |
60–90 μm | % | 1.35 | 1.33 | |
30–60 μm | % | 1.95 | 4.25 | |
20–30 μm | % | 1.30 | 3.85 | |
P2 | 10–20 μm | % | 2.32 | 7.89 |
1–10 μm | % | 43.56 | 43.95 | |
0.5–1 μm | % | 16.20 | 14.04 | |
P1 | 0.25–0.5 μm | % | 10.28 | 7.23 |
0.1–0.25 μm | % | 8.45 | 5.84 | |
0.05–0.1 μm | % | 5.23 | 4.00 | |
P0 | 0.025–0.05 μm | % | 1.79 | 1.45 |
0.01–0.025 μm | % | 1.33 | 0.75 | |
0.006–0.01 μm | % | 0.03 | 0.00 |
Compressive strength class of mortar [MPa] | fm [MPa] | fmx [MPa] | fm,t [MPa] |
---|---|---|---|
M15 | 15 | 3.5 | 1.98 |
M10 | 10 | 2.5 | 1.43 |
M5 | 5 | 1.6 | 0.95 |
M2.5 | 2.5 | 0.8 | 0.48 |