<abstract xmlns="http://www.w3.org/1999/xhtml">A thermal decomposition of a cobalt-lanthanum catalyst precursor containing a mixture of cobalt and lanthanum compounds obtained by co-precipitation were studied using thermal analysis coupled with mass spectrometry (TG-MS). Studies revealed that the calcination in air at 500°C is sufficient to transform the obtained cobalt precipitate into Co3O4, but it leads to only partial decomposition of lanthanum precipitate. In order to obtain Co/La catalyst precursor containing La2O3 the calcination in air at the temperature about 800°C is required. However, it is unfavorable from the point of view of textural properties of the catalyst precursor. A strong effect of storage conditions on the phase composition of the studied cobalt-lanthanum catalyst precursor, caused by the formation of lanthanum hydroxide and lanthanum carbonates from La2O3 when contacting with air, was observed.</abstract>

A thermal decomposition of a cobalt-lanthanum catalyst precursor containing a mixture of cobalt and lanthanum compounds obtained by co-precipitation were studied using thermal analysis coupled with mass spectrometry (TG-MS). Studies revealed that the calcination in air at 500°C is sufficient to transform the obtained cobalt precipitate into Co3O4, but it leads to only partial decomposition of lanthanum precipitate. In order to obtain Co/La catalyst precursor containing La2O3 the calcination in air at the temperature about 800°C is required. However, it is unfavorable from the point of view of textural properties of the catalyst precursor. A strong effect of storage conditions on the phase composition of the studied cobalt-lanthanum catalyst precursor, caused by the formation of lanthanum hydroxide and lanthanum carbonates from La2O3 when contacting with air, was observed.

Cobalt-lanthanum catalyst precursors for ammonia synthesis: determination of calcination temperature and storage conditions

Polish Journal of Chemical Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

A thermal decomposition of a cobalt-lanthanum catalyst precursor containing a mixture of cobalt and lanthanum compounds obtained by co-precipitation were...

Cobalt-lanthanum catalyst precursors for ammonia synthesis: determination of calcination temperature and storage conditions

Online veröffentlicht: 08. Juli 2017

Seitenbereich: 61 - 66

DOI: https://doi.org/10.1515/pjct-2017-0029

Schlüsselwörter
ammonia synthesis, catalyst precursor, cobalt, lanthanum, thermal analysis

© 2017 Magdalena Zybert et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Cobalt-lanthanum catalyst precursors for ammonia synthesis: determination of calcination temperature and storage conditions

Online veröffentlicht: 08. Juli 2017

Seitenbereich: 61 - 66

DOI: https://doi.org/10.1515/pjct-2017-0029

Schlüsselwörterammonia synthesis, catalyst precursor, cobalt, lanthanum, thermal analysis

© 2017 Magdalena Zybert et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
ammonia synthesis, catalyst precursor, cobalt, lanthanum, thermal analysis