<abstract xmlns="http://www.w3.org/1999/xhtml">In this study, ultrasonic treatment of baker’s yeast effluent was investigated in an ultrasonic homogenizer emitting waves at 20 kHz. The SnO2/TiO2 composites were used as a sonocatalyst to assist the sonication process. Decolorization and chemical oxygen demand (COD) removal of baker’s yeast effluent with ultrasonic irradiation was examined. The effect of the composite preparation method, the molar ratio of SnO2/TiO2, mixing time while the composite was prepared, the calcination temperature and time, the catalyst amount were investigated. The decolorization was higher at a 4:1 molar ratio of the SnO2/TiO2 composite prepared by using an ultrasonic probe and 6 min ultrasonic irradiation time. The decolorization increased, with an increase in the calcination temperature. The optimum calcination time was 60 min and catalyst amount was 0.2 g/l. According to the results, decolorization rate was 26.63% using this composite. There was no COD removal at the studied conditions.</abstract>

In this study, ultrasonic treatment of baker’s yeast effluent was investigated in an ultrasonic homogenizer emitting waves at 20 kHz. The SnO2/TiO2 composites were used as a sonocatalyst to assist the sonication process. Decolorization and chemical oxygen demand (COD) removal of baker’s yeast effluent with ultrasonic irradiation was examined. The effect of the composite preparation method, the molar ratio of SnO2/TiO2, mixing time while the composite was prepared, the calcination temperature and time, the catalyst amount were investigated. The decolorization was higher at a 4:1 molar ratio of the SnO2/TiO2 composite prepared by using an ultrasonic probe and 6 min ultrasonic irradiation time. The decolorization increased, with an increase in the calcination temperature. The optimum calcination time was 60 min and catalyst amount was 0.2 g/l. According to the results, decolorization rate was 26.63% using this composite. There was no COD removal at the studied conditions.

Ultrasonic treatment of baker’s yeast effluent using SnO2/TiO2 composite

Department of Chemical Engineering, Faculty of Engineering

Polish Journal of Chemical Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Ultrasonic treatment of baker’s yeast effluent using SnO/TiO composite

In this study, ultrasonic treatment of baker’s yeast effluent was investigated in an ultrasonic homogenizer emitting waves at 20 kHz. The SnO2/TiO2 composites...

Ultrasonic treatment of baker’s yeast effluent using SnO₂/TiO₂ composite

Online veröffentlicht: 08. Juli 2017

Seitenbereich: 26 - 32

DOI: https://doi.org/10.1515/pjct-2017-0023

Schlüsselwörter
Baker’s yeast effluent, COD, decolorization, sonolysis, ultrasonic irradiation

© 2017 Didem Ildirar et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Ultrasonic treatment of baker’s yeast effluent using SnO2/TiO2 composite

Online veröffentlicht: 08. Juli 2017

Seitenbereich: 26 - 32

DOI: https://doi.org/10.1515/pjct-2017-0023

SchlüsselwörterBaker’s yeast effluent, COD, decolorization, sonolysis, ultrasonic irradiation

© 2017 Didem Ildirar et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Ultrasonic treatment of baker’s yeast effluent using SnO₂/TiO₂ composite

Schlüsselwörter
Baker’s yeast effluent, COD, decolorization, sonolysis, ultrasonic irradiation