<abstract xmlns="http://www.w3.org/1999/xhtml"> In this research, we studied the magnetic phase transition by Mössbauer spectroscopy and using vibrating sample magnetometer for amorphous Fe86-xZr7CrxNb2Cu1B4 (x = 0 or 6) alloys in the as-quenched state and after accumulative annealing in the temperature range 600-750 K. The Mössbauer investigations were carried out at room and nitrogen temperatures. The Mössbauer spectra of the investigated alloys at room temperature are characteristic of amorphous paramagnets and have a form of asymmetric doublets. However, at nitrogen temperature, the alloys behave like ferromagnetic amorphous materials. The two components are distinguished in the spectrum recorded at both room and nitrogen temperatures. The low field component in the distribution of hyperfine field induction shifts towards higher field with the annealing temperature. It is assumed that during annealing at higher temperature, due to diffusion processes, the grains of α-Fe are created in the area corresponding to this component. Both investigated alloys show the invar effect and the decrease of hyperfine field induction after annealing at 600 K for 10 min is observed. It is accompanied by the lowering of Curie temperature. </abstract>

In this research, we studied the magnetic phase transition by Mössbauer spectroscopy and using vibrating sample magnetometer for amorphous Fe86-xZr7CrxNb2Cu1B4 (x = 0 or 6) alloys in the as-quenched state and after accumulative annealing in the temperature range 600-750 K. The Mössbauer investigations were carried out at room and nitrogen temperatures. The Mössbauer spectra of the investigated alloys at room temperature are characteristic of amorphous paramagnets and have a form of asymmetric doublets. However, at nitrogen temperature, the alloys behave like ferromagnetic amorphous materials. The two components are distinguished in the spectrum recorded at both room and nitrogen temperatures. The low field component in the distribution of hyperfine field induction shifts towards higher field with the annealing temperature. It is assumed that during annealing at higher temperature, due to diffusion processes, the grains of α-Fe are created in the area corresponding to this component. Both investigated alloys show the invar effect and the decrease of hyperfine field induction after annealing at 600 K for 10 min is observed. It is accompanied by the lowering of Curie temperature.

Hyperfine interactions and some thermomagnetic properties of amorphous FeZr(Cr)NbBCu alloys

Nukleonika

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

In this research, we studied the magnetic phase transition by Mössbauer spectroscopy and using vibrating sample magnetometer for amorphous Fe86-xZr7CrxNb2Cu1B4...

Hyperfine interactions and some thermomagnetic properties of amorphous FeZr(Cr)NbBCu alloys

Online veröffentlicht: 09. Juni 2017

Seitenbereich: 135 - 140

Eingereicht: 21. Juni 2016

Akzeptiert: 29. Sept. 2016

DOI: https://doi.org/10.1515/nuka-2017-0019

Schlüsselwörter
amorphous Fe-based alloys, invar effect, Mössbauer spectroscopy

© by Agnieszka Łukiewska

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Hyperfine interactions and some thermomagnetic properties of amorphous FeZr(Cr)NbBCu alloys

Online veröffentlicht: 09. Juni 2017

Seitenbereich: 135 - 140

Eingereicht: 21. Juni 2016

Akzeptiert: 29. Sept. 2016

DOI: https://doi.org/10.1515/nuka-2017-0019

Schlüsselwörteramorphous Fe-based alloys, invar effect, Mössbauer spectroscopy

© by Agnieszka Łukiewska

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Schlüsselwörter
amorphous Fe-based alloys, invar effect, Mössbauer spectroscopy