<abstract xmlns="http://www.w3.org/1999/xhtml"> Microstructure and thermomagnetic characteristics of the amorphous Fe51Co12Si16B8Mo5P8 alloy in the as-quenched state and after 1 h of annealing at 573 K and 773 K are studied. The structural investigations performed by Mössbauer spectroscopy and X-ray diffractometry confirmed the amorphous structure of the analysed materials. An increase in the annealing temperature up to 773 K does not lead to crystallization of the amorphous alloy. Only structural rearrangement that causes changes in the topological short-range order and annealing out of free volume is observed. This behaviour was confirmed by modifications of the shapes of hyperfine field distributions derived from the corresponding Mössbauer spectra of the investigated alloys. The Curie temperatures of the as-quenched and annealed Fe51Co12Si16B8Mo5P8 alloy at 573 and 773 K are 400, 405 and 421 K, respectively.</abstract>

Microstructure and thermomagnetic characteristics of the amorphous Fe51Co12Si16B8Mo5P8 alloy in the as-quenched state and after 1 h of annealing at 573 K and 773 K are studied. The structural investigations performed by Mössbauer spectroscopy and X-ray diffractometry confirmed the amorphous structure of the analysed materials. An increase in the annealing temperature up to 773 K does not lead to crystallization of the amorphous alloy. Only structural rearrangement that causes changes in the topological short-range order and annealing out of free volume is observed. This behaviour was confirmed by modifications of the shapes of hyperfine field distributions derived from the corresponding Mössbauer spectra of the investigated alloys. The Curie temperatures of the as-quenched and annealed Fe51Co12Si16B8Mo5P8 alloy at 573 and 773 K are 400, 405 and 421 K, respectively.

Microstructure and magnetic properties of amorphous Fe51Co12Si16B8Mo5P8 alloy

Nukleonika

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Microstructure and magnetic properties of amorphous FeCoSiBMoP alloy

Microstructure and thermomagnetic characteristics of the amorphous Fe51Co12Si16B8Mo5P8 alloy in the as-quenched state and after 1 h of annealing at 573 K and...

Microstructure and magnetic properties of amorphous Fe₅₁Co₁₂Si₁₆B₈Mo₅P₈ alloy

Online veröffentlicht: 09. Juni 2017

Seitenbereich: 85 - 89

Eingereicht: 18. Juli 2016

Akzeptiert: 14. Okt. 2016

DOI: https://doi.org/10.1515/nuka-2017-0011

Schlüsselwörter
microstructure, Mössbauer spectroscopy, magnetic properties, Curie point

© by Mariusz Hasiak

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Microstructure and magnetic properties of amorphous Fe51Co12Si16B8Mo5P8 alloy

Online veröffentlicht: 09. Juni 2017

Seitenbereich: 85 - 89

Eingereicht: 18. Juli 2016

Akzeptiert: 14. Okt. 2016

DOI: https://doi.org/10.1515/nuka-2017-0011

Schlüsselwörtermicrostructure, Mössbauer spectroscopy, magnetic properties, Curie point

© by Mariusz Hasiak

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Microstructure and magnetic properties of amorphous Fe₅₁Co₁₂Si₁₆B₈Mo₅P₈ alloy

Schlüsselwörter
microstructure, Mössbauer spectroscopy, magnetic properties, Curie point