<abstract xmlns="http://www.w3.org/1999/xhtml">The influence of sandblasting on surface and subsurface of stainless steel is investigated using variable energy positron beam (VEP), positron annihilation spectroscopy (PAS), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Samples of stainless steel were blasted using 110 μm particles of Al2O3 under different pressure and time duration. In the case of sandblasting for 90 s, the reduction of positron diffusion length depending on the applied pressure was observed. Sandblasting during 30 s leads only to the reduction of positron diffusion length to about 60 nm for all samples. Positron lifetimes close to 170 ps measured using positrons emitted directly from the source point to the presence of vacancies on the dislocation lines. SEM and AFM images show that surface roughness depends rather on pressure of sandblasting than time of exposition.</abstract>

The influence of sandblasting on surface and subsurface of stainless steel is investigated using variable energy positron beam (VEP), positron annihilation spectroscopy (PAS), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Samples of stainless steel were blasted using 110 μm particles of Al2O3 under different pressure and time duration. In the case of sandblasting for 90 s, the reduction of positron diffusion length depending on the applied pressure was observed. Sandblasting during 30 s leads only to the reduction of positron diffusion length to about 60 nm for all samples. Positron lifetimes close to 170 ps measured using positrons emitted directly from the source point to the presence of vacancies on the dislocation lines. SEM and AFM images show that surface roughness depends rather on pressure of sandblasting than time of exposition.

Studies of stainless steel exposed to sandblasting

Joint Institute for Nuclear Research, 6 Joliot Curie Str., 141980 Dubna, Moscow region, Russian Federation and Institute of Nuclear Physics of the Polish Academy of Sciences, 152 Radzikowskiego Str., 31-342 Kraków, Poland

Northern Arctic Federal University, 163002 Severnaya Dvina Emb. 17, Arkhangelsk, Russian Federation

Joint Institute for Nuclear Research, 6 Joliot Curie Str., 141980 Dubna, Moscow region, Russian Federation and Institute of Electrophysics and Radiation Technologies NAS of Ukraine, 28 Chernyshevsky Str., 61002 Kharkov, Ukraine

Nukleonika

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Studies of stainless steel exposed to sandblasting"}

The influence of sandblasting on surface and subsurface of stainless steel is investigated using variable energy positron beam (VEP), positron annihilation...

Studies of stainless steel exposed to sandblasting

Online veröffentlicht: 01. Dez. 2015

Seitenbereich: 721 - 724

Eingereicht: 19. Juni 2015

Akzeptiert: 31. Aug. 2015

DOI: https://doi.org/10.1515/nuka-2015-0129

Schlüsselwörter
stainless steel, sandblasting, defects, positron beam

© 2015 Paweł Horodek et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Studies of stainless steel exposed to sandblasting

Online veröffentlicht: 01. Dez. 2015

Seitenbereich: 721 - 724

Eingereicht: 19. Juni 2015

Akzeptiert: 31. Aug. 2015

DOI: https://doi.org/10.1515/nuka-2015-0129

Schlüsselwörterstainless steel, sandblasting, defects, positron beam

© 2015 Paweł Horodek et al., published by De Gruyter Open

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
stainless steel, sandblasting, defects, positron beam