<abstract xmlns="http://www.w3.org/1999/xhtml">This paper deals with the luminescence of silica (KV-type) induced by beam of hydrogen ions with the energy of 210 keV per nucleon. An average implantation dose of up to 3.5 × 1021 cm−3 (5 × 1010 Gy) was accumulated during irradiation over an extended period. The luminescent spectra consisted of the blue band (maximum at 456 nm) and the red band (650 nm) in the visible range. It was shown that increase in the absorption dose had an effect on the silica luminescence. It was found that the most significant changes in the spectrum occurred during the dose accumulation in the region of 550–700 nm. The shape of the spectrum of the luminescent radiation in this wavelength range was affected both by the oxygen deficient centres (blue band) and non-bridging oxygen hole centers (red band). Mathematical processing of the experimental spectra permitted to identify contributions to the luminescent radiation coming from both types of defects.</abstract>

This paper deals with the luminescence of silica (KV-type) induced by beam of hydrogen ions with the energy of 210 keV per nucleon. An average implantation dose of up to 3.5 × 1021 cm−3 (5 × 1010 Gy) was accumulated during irradiation over an extended period. The luminescent spectra consisted of the blue band (maximum at 456 nm) and the red band (650 nm) in the visible range. It was shown that increase in the absorption dose had an effect on the silica luminescence. It was found that the most significant changes in the spectrum occurred during the dose accumulation in the region of 550–700 nm. The shape of the spectrum of the luminescent radiation in this wavelength range was affected both by the oxygen deficient centres (blue band) and non-bridging oxygen hole centers (red band). Mathematical processing of the experimental spectra permitted to identify contributions to the luminescent radiation coming from both types of defects.

Change of silica luminescence due to fast hydrogen ion bombardment

V. N. Karazin Kharkiv National University, 31 Kurchatov Ave., 61108 Kharkiv, Ukraine, Tel./Fax: +38 057 335 3610

Nukleonika

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

{"article-title":"Change of silica luminescence due to fast hydrogen ion bombardment"}

This paper deals with the luminescence of silica (KV-type) induced by beam of hydrogen ions with the energy of 210 keV per nucleon. An average implantation...

Change of silica luminescence due to fast hydrogen ion bombardment

Online veröffentlicht: 22. Juni 2015

Seitenbereich: 289 - 292

Eingereicht: 16. Juni 2014

Akzeptiert: 01. Apr. 2014

DOI: https://doi.org/10.1515/nuka-2015-0063

Schlüsselwörter
luminescent spectrum, absorption dose, ion implantation, silica

© Vitaliy P. Zhurenko et al.

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Change of silica luminescence due to fast hydrogen ion bombardment

Online veröffentlicht: 22. Juni 2015

Seitenbereich: 289 - 292

Eingereicht: 16. Juni 2014

Akzeptiert: 01. Apr. 2014

DOI: https://doi.org/10.1515/nuka-2015-0063

Schlüsselwörterluminescent spectrum, absorption dose, ion implantation, silica

© Vitaliy P. Zhurenko et al.

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Schlüsselwörter
luminescent spectrum, absorption dose, ion implantation, silica