<abstract xmlns="http://www.w3.org/1999/xhtml">(BiFeO3)1-<italic>x</italic>-(BaTiO3)<italic>x</italic> solid solutions with <italic>x</italic> = 0.1–0.4 and 0.7 were investigated. The ceramics were prepared by mechanical activation technology and subsequent heat treatment. As was proved by X-ray diffraction, increase of BaTiO3 concentration causes a change in the crystalline structure from the rhombohedral structure characteristic of BiFeO3 to a cubic one. 57Fe Mössbauer spectroscopy allowed observation of a gradual transformation from an ordered spin structure of Fe3+ ions to the paramagnetic state with an increase of <italic>x</italic>.</abstract>

(BiFeO3)1-x-(BaTiO3)x solid solutions with x = 0.1–0.4 and 0.7 were investigated. The ceramics were prepared by mechanical activation technology and subsequent heat treatment. As was proved by X-ray diffraction, increase of BaTiO3 concentration causes a change in the crystalline structure from the rhombohedral structure characteristic of BiFeO3 to a cubic one. 57Fe Mössbauer spectroscopy allowed observation of a gradual transformation from an ordered spin structure of Fe3+ ions to the paramagnetic state with an increase of x.

Structure and Mössbauer spectroscopy studies of mechanically activated (BiFeO3)1−x-(BaTiO3)x solid solutions

Institute of Electronics and Information Technology, Lublin University of Technology, 38A Nadbystrzycka Str., 20-618 Lublin, Poland and Department and Division of Nuclear Medicine, Lublin University of Medicine, 8 Jaczewskiego Str., 20-954 Lublin, Poland

Faculty of Materials Science and Engineering, Warsaw University of Technology, 141 Wołoska Str., 02-507 Warsaw, Poland

Institute of Electronics and Information Technology, Lublin University of Technology, 38A Nadbystrzycka Str., 20-618 Lublin, Poland, Tel.: +48 81 538 4503, Fax: +48 81 538 4312

Nukleonika

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Structure and Mössbauer spectroscopy studies of mechanically activated (BiFeO)-(BaTiO) solid solutions

(BiFeO3)1-x-(BaTiO3)x solid solutions with x = 0.1–0.4 and 0.7 were investigated. The ceramics were prepared by mechanical activation technology and subsequent...

Structure and Mössbauer spectroscopy studies of mechanically activated (BiFeO₃)_1−x-(BaTiO₃)_x solid solutions

Online veröffentlicht: 12. März 2015

Seitenbereich: 109 - 114

Eingereicht: 18. Juni 2014

Akzeptiert: 02. Nov. 2014

DOI: https://doi.org/10.1515/nuka-2015-0022

Schlüsselwörter
ceramic solid solutions, hyperfine interactions, mechanical activation, Mössbauer spectroscopy

© Bożena Malesa, Anna Antolak-Dudka, Dariusz Oleszak, Tomasz Pikula

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Structure and Mössbauer spectroscopy studies of mechanically activated (BiFeO3)1−x-(BaTiO3)x solid solutions

Online veröffentlicht: 12. März 2015

Seitenbereich: 109 - 114

Eingereicht: 18. Juni 2014

Akzeptiert: 02. Nov. 2014

DOI: https://doi.org/10.1515/nuka-2015-0022

Schlüsselwörterceramic solid solutions, hyperfine interactions, mechanical activation, Mössbauer spectroscopy

© Bożena Malesa, Anna Antolak-Dudka, Dariusz Oleszak, Tomasz Pikula

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Structure and Mössbauer spectroscopy studies of mechanically activated (BiFeO₃)_1−x-(BaTiO₃)_x solid solutions

Schlüsselwörter
ceramic solid solutions, hyperfine interactions, mechanical activation, Mössbauer spectroscopy