<abstract xmlns="http://www.w3.org/1999/xhtml"><p> The aim of this research was to study the properties of nanohydroxyapatite (nanoHAp) and nanohydroxyapatite, doped with nanosilver (nanoHAp/nanoAg), coatings obtained by an electrophoretic deposition process. The suspensions was prepared by dispersing 0.1 g of HAp nanopowder for nanoHAp coatings and 0.1 g of nanoHAp and 0.025 g nanoAg for nanoHAp/nanoAg coatings. The deposition was carried out for 1 min at 50 V voltage followed by drying at room temperature for 24 h and heating at 800°C for 1 h in vacuum. The thickness of the nanoHAp and nanoHAp/nanoAg coatings was found as of about 5 μm. The corrosion behavior tests made by potentiodynamic methods brought out slightly higher values of corrosion current for nanoHAp coatings and nanoHAp/nanoAg coatings as compared to the reference Ti13Zr13Nb specimen. The nanohardness of the nanoHAp coatings achieved 0.020 ± 0.004 GPa and of the nanoHAp/nanoAg coatings 0.026 ± 0.012 GPa. Nanoscratch test of the nanoHAp and nanoHAp/nanoAg coatings revealed an increased Critical Friction (mN) in the presence of nanosilver particles. The wettability angles decreased for nanoHAp/nanoAg coatings comparing to pure nanoHAp coatings on titanium alloy.</p></abstract>

The aim of this research was to study the properties of nanohydroxyapatite (nanoHAp) and nanohydroxyapatite, doped with nanosilver (nanoHAp/nanoAg), coatings obtained by an electrophoretic deposition process. The suspensions was prepared by dispersing 0.1 g of HAp nanopowder for nanoHAp coatings and 0.1 g of nanoHAp and 0.025 g nanoAg for nanoHAp/nanoAg coatings. The deposition was carried out for 1 min at 50 V voltage followed by drying at room temperature for 24 h and heating at 800°C for 1 h in vacuum. The thickness of the nanoHAp and nanoHAp/nanoAg coatings was found as of about 5 μm. The corrosion behavior tests made by potentiodynamic methods brought out slightly higher values of corrosion current for nanoHAp coatings and nanoHAp/nanoAg coatings as compared to the reference Ti13Zr13Nb specimen. The nanohardness of the nanoHAp coatings achieved 0.020 ± 0.004 GPa and of the nanoHAp/nanoAg coatings 0.026 ± 0.012 GPa. Nanoscratch test of the nanoHAp and nanoHAp/nanoAg coatings revealed an increased Critical Friction (mN) in the presence of nanosilver particles. The wettability angles decreased for nanoHAp/nanoAg coatings comparing to pure nanoHAp coatings on titanium alloy.

The Properties of Nanosilver – Doped Nanohydroxyapatite Coating On the Ti13zr13Nb Alloy

Advances in Materials Science

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The aim of this research was to study the properties of nanohydroxyapatite (nanoHAp) and nanohydroxyapatite, doped with nanosilver (nanoHAp/nanoAg), coatings...

The Properties of Nanosilver – Doped Nanohydroxyapatite Coating On the Ti13zr13Nb Alloy

Online veröffentlicht: 01. Aug. 2017

Seitenbereich: 18 - 28

DOI: https://doi.org/10.1515/adms-2017-0008

Schlüsselwörter
nanohydroxyapatite coatings, nanosilver, titanium alloy, electrophoretic deposition

© by M. Bartmanski

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

The Properties of Nanosilver – Doped Nanohydroxyapatite Coating On the Ti13zr13Nb Alloy

Online veröffentlicht: 01. Aug. 2017

Seitenbereich: 18 - 28

DOI: https://doi.org/10.1515/adms-2017-0008

Schlüsselwörternanohydroxyapatite coatings, nanosilver, titanium alloy, electrophoretic deposition

© by M. Bartmanski

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 License.

Schlüsselwörter
nanohydroxyapatite coatings, nanosilver, titanium alloy, electrophoretic deposition