<abstract xml:lang="en" xmlns="http://www.w3.org/1999/xhtml"><p>Strontium hexaferrite thin films have been grown on glass substrates at room temperature in oxygen environment by pulsed laser deposition method. The effect of oxygen pressure (po2) on the structural and magnetic properties has been investigated. The as-deposited films were found to be amorphous in nature. The crystallization of these films was achieved by annealing at a temperature of 850 °C in air. The thickness of the film increased with po2. The film grown at po2 = 0.455 Pa had a clear hexagonal structure. The values of coercivity for the films were found to increase with po2.</p></abstract>

Strontium hexaferrite thin films have been grown on glass substrates at room temperature in oxygen environment by pulsed laser deposition method. The effect of oxygen pressure (po2) on the structural and magnetic properties has been investigated. The as-deposited films were found to be amorphous in nature. The crystallization of these films was achieved by annealing at a temperature of 850 °C in air. The thickness of the film increased with po2. The film grown at po2 = 0.455 Pa had a clear hexagonal structure. The values of coercivity for the films were found to increase with po2.

Effect of low oxygen pressure on structural and magnetic properties of quenched SrFe12O19 thin films

Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Science, Ningbo, Zhejiang, 31520, P.R. China

Materials Research Centre, Indian Institute of Science, Bangalore, 560012, India

School of Physics, University of Hyderabad, Hyderabad, 500046, India

Materials Science-Poland

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Strontium hexaferrite thin films have been grown on glass substrates at room temperature in oxygen environment by pulsed laser deposition method. The effect of...

Effect of low oxygen pressure on structural and magnetic properties of quenched SrFe12O19 thin films

Published Online: Dec 15, 2013

Page range: 581 - 586

DOI: https://doi.org/10.2478/s13536-013-0142-4

Keywords
thin films, pulsed laser deposition, hexaferrites, magnetic properties

© 2013 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Effect of low oxygen pressure on structural and magnetic properties of quenched SrFe12O19 thin films

Published Online: Dec 15, 2013

Page range: 581 - 586

DOI: https://doi.org/10.2478/s13536-013-0142-4

Keywordsthin films, pulsed laser deposition, hexaferrites, magnetic properties

© 2013 Wroclaw University of Technology

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Keywords
thin films, pulsed laser deposition, hexaferrites, magnetic properties